Magnesium-based thermoelectric (TE) materials have attracted considerable interest due to their high ZT values, coupled with their low cost, widespread availability, nontoxicity, and low density. In this review, we provide a succinct overview of the advances and strategies pertaining to the development of Mg-based materials aimed at enhancing their performance. Following this, we delve into the major challenges posed by the severe working conditions, such as high temperature and thermal cycling, which adversely impact the behavior and long-term stability of the TE modules. Challenges include issues like the lack of mechanical strength, chemical instability, and unreliable contact. Subsequently, we focus on the key methodologies aimed at addressing these challenges to facilitate the broader application of the TE modules. These include boosting the mechanical strength, especially the toughness, through grain refining and additions of second phases. Furthermore, strategies targeted at enhancing the chemical stability through coatings and modifying the microstructure, as well as improving the contact design and materials, are discussed. In the end, we highlight the perspectives for boosting the practical applications of Mg-based TE materials in the future.

Due to their relatively low cost, large surface area and good chemical and physical properties, carbon nanofibers (CNFs) are attractive for the fabrication of electrodes for supercapacitors (SCs). However, their relatively low electrical conductivity has impeded their practical application. To this end, a novel active-screen plasma activation and deposition technology has been developed to deposit silver, platinum and palladium nanoparticles on activated CNFs surfaces to increase their specific surface area and electrical conductivity, thus improving the specific capacitance. The functionalised CNFs were fully characterised using scanning electron microscope (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffraction (XRD) and their electrochemical properties were evaluated using cyclic voltammetry and electrochemical impedance spectroscopy. The results showed a significant improvement in specific capacitance, as well as electrochemical impedance over the untreated CNFs. The functionalisation of CNFs via environmental-friendly active-screen plasma technology provides a promising future for cost-effective supercapacitors with high power and energy density.

A polyamide (PA) 12-based thermoplastic composite was modified with carbon nanotubes (CNTs), CNTs grafted onto chopped carbon fibers (CFs), and graphene nanoplatelets (GNPs) with CNTs to improve its thermal conductivity for application as a heat sink in electronic components. The carbon-based nanofillers were examined by SEM and Raman. The laser flash method was used to measure the thermal diffusivity in order to calculate the thermal conductivity. Electrical conductivity measurements were made using a Keithley 6517B electrometer in the 2-point mode. The composite structure was examined by SEM and micro-CT. PA12 with 15 wt% of GNPs and 1 wt% CNTs demonstrated the highest thermal conductivity, and its processability was investigated, utilizing sequential interdependence tests to evaluate the composite material behavior during fused filament fabrication (FFF) 3D printing processing. Through this assessment, selected printing parameters were investigated to determine the optimum parametric combination and processability window for the composite material, revealing that the selected composition meets the necessary criteria to be processable with FFF.

In this work, different amounts of CNFs were added into a complex formulation to coat the CFs surfaces via sizing in order to enhance the bonding between the fibre and the resin in the CF-reinforced polymer composites. The sized CFs bundles were characterised by SEM and Raman. The nanomechanical properties of the composite materials produced were assessed by the nanoindentation test. The interfacial properties of the fibre and resin were evaluated by a push-out method developed on nanoindentation. The average interfacial shear strength of the fibre/matrix interface could be calculated by the critical load, sheet thickness and fibre diameter. The contact angle measurements and resin spreadability were performed prior to nanoindentation to investigate the wetting properties of the fibre. After the push-out tests, the characterisation via optical microscopy/SEM was carried out to ratify the results. It was found the CFs sizing with CNFs (1 to 10 wt%) could generally increase the interfacial shear strength but it was more cost-effective with a small amount of evenly distributed CNFs on CFs.

Three multifunctional smart composites for next-generation applications have been studied differently through versatile nanoindentation investigation techniques. They are used in order to determine peculiarities and specific properties for the different composites and to study the charge/matrix, charge/surface, or smart functions interactions. At first, a mapping indentation test was used to check the distribution of hardness and modulus across a large region to examine any non-uniformity due to structural anomalies or changes in properties for a carbon nanotubes (CNTs)-reinforced polypropylene (PP V-2) nanocomposite. This smart composite is suitable to be used in axial impeller fans and the results can be used to improve the process of the composite produced by injection moulding. Secondly, the interfacial properties of the carbon fibre (CF) and the resin were evaluated by a push-out method utilizing the smaller indentation tip to target the individual CF and apply load to measure its displacement under loads. This is useful to evaluate the effectiveness of the surface modification on the CFs, such as sizing. Finally, nanoindentation at different temperatures was used for the probing of the in situ response of smart shape memory polymer composite (SMPC) usable in grabbing devices for aerospace applications. Furthermore, the triggering temperature of the shape memory polymer response can be determined by observing the change of indentations after the heating and cooling cycles.