Titanium oxide layers were produced via a novel catalytic ceramic conversion treatment (CCCT, C3T) on Ti-6Al-4V. This CCCT process is carried out by applying thin catalytic films of silver and palladium onto the substrate before an already established traditional ceramic conversion treatment (CCT, C2T) is carried out. The layers were characterised using scanning electron microscopy, X-ray diffraction, transmission electron microscopy; surface micro-hardness and reciprocating tribological performance was assessed; antibacterial performance was also assessed with S. aureus. This CCCT has been shown to increase the oxide thickness from ~5 to ~100 µm, with the production of an aluminium rich layer and agglomerates of silver and palladium oxide surrounded by vanadium oxide at the surface. The wear factor was significantly reduced from ~393 to ~5 m³/N·m, and a significant reduction in the number of colony-forming units per ml of Staphylococcus aureus on the CCCT surfaces was observed. The potential of the novel C3T treatment has been demonstrated by comparing the performance of C3T treated and untreated Ti6Al4V fixation pins through inserting into simulated bone materials.

Zr and its alloys are widely used in multiple areas, including the nuclear and medical fields. Previous studies indicate that a ceramic conversion treatment (C2T) of Zr-based alloys can address the issues of low hardness, high friction, and poor wear resistance of Zr based alloys. This paper introduced a novel catalytic ceramic conversion treatment (C3T) to Zr702 by pre-depositing a catalytic film (such as silver, gold, platinum, etc.) before the ceramic conversion treatment, which efficiently promoted the C2T process, in terms of reduced treatment times, with a thick, good quality, surface ceramic layer. The formed ceramic layer significantly improved the surface hardness and tribological properties of Zr702 alloy. Compared with conventional C2T, the C3T technique provided two orders of magnitude reduction of wear factor and reduced the coefficient of friction from 0.65 to <0.25. Among the C3T samples, the C3TAg and the C3TAu samples have the highest wear resistance and lowest CoF, mainly due to the self-lubricant formation during the wear processes.