The fabrication of skin-care products with therapeutic properties has been significant for human health trends. In this study, we developed efficient hydrophilic composite nanofibers (NFs) loaded with the folic acid (FA) by electrospinning and electrospraying processes for tissue engineering or wound healing cosmetic applications. The morphological, chemical and thermal characteristics, in vitro release properties, and cytocompatibility of the resulting composite fibers with the same amount of folic acid were analyzed. The SEM micrographs indicate that the obtained nanofibers were in the nanometer range, with an average fiber diameter of 75–270 nm and a good porosity ratio (34–55%). The TGA curves show that FA inhibits the degradation of the polymer and acts as an antioxidant at high temperatures. More physical interaction between FA and matrices has been shown to occur in the electrospray process than in the electrospinning process. A UV-Vis in vitro study of FA-loaded electrospun fibers for 8 h in artificial acidic (pH 5.44) and alkaline (pH 8.04) sweat solutions exhibited a rapid release of FA-loaded electrospun fibers, showing the effect of polymer matrix–FA interactions and fabrication processes on their release from the nanofibers. PVA-CHi/FA webs have the highest release value, with 95.2% in alkaline media. In acidic media, the highest release (92%) occurred on the PVA-Gel–CHi/sFA sample, and this followed first-order and Korsmeyer–Peppas kinetic models. Further, the L929 cytocompatibility assay results pointed out that all NFs (with/without FA) generated had no cell toxicity; on the contrary, the FA in the fibers facilitates cell growth. Therefore, the nanofibers are a potential candidate material in skin-care and tissue engineering applications.

In this study, hydrophilic based bioactive nanofibers were produced via an electrospinning and electrospraying simultaneous process. Poly(vinyl alcohol) (PVA), poly(vinyl alcohol)-gelatin (PVA-Gel), and poly(vinyl alcohol)-alginate (PVA-Alg) polymers were used as the matrix material and folic acid (FA) particles were dispersed simultaneously on the surface of the nanofibers. The morphology of the nanofibers (NFs) was uniform and confirmed by scanning electron microscopy. Thermal behavior, chemical structure of the composite nanofibers were investigated by thermogravimetric analysis, and Attenuated Total Reflectance-Fourier Transform Infrared Spectroscopy which showed that no chemical bonding between vitamin and polymers. A fast release of FA-loaded electrospun fibers was carried out by UV-Vis in vitro study within the 8 hour-period in artificial sweat solutions (pH 5.44). The obtained PVA/FA, PVA-Gel/FA, and PVA-Alg/FA fibers released 49.6%, 69.55%, and 50.88% of the sprayed FA in 8 h, indicating the influence of polymer matrix and polymer-drug interactions, on its release from the polymer matrix. Moreover, biocompatibility of all developed novel NFs was assessed by two different cytotoxicity tests, 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay and neutral red uptake (NRU) assay in L929 (mouse fibroblasts) cell lines. In all cases, it is concluded that these new electrospun fibers had fast-release of the vitamin and the hybrid process is suitable for transdermal patch applications, especially for skin-care products. The results of cytocompatibility assays on L929 reveal that all prepared NFs have no or slight cell toxicity. PVA and PVA-Gel with/without FA nanofibers seems more biocompatible than PVA-Alg nanofibers.

In this study, sustainable water-based films were produced via the solvent-casting method. Petroleum-free-based polyvinyl alcohol (PVA) and carbohydrate-based inulin (INL) were used as matrices. Vegetable-waste pumpkin powder was used in the study because of its sustainability and antibacterial properties. Pickering emulsions were prepared using β-cyclodextrin. The influence of the different ratios of the β-cyclodextrin/niaouli essential oil (β-CD/NEO) inclusion complex (such as 1:1, 1:3, and 1:5) on the morphological (SEM), thermal (TGA), physical (FT-IR), wettability (contact angle), and mechanical (tensile test) characteristics of PVA/inulin films were investigated. Moreover, the antibacterial activities against the Gram (−) (Escherichia coli and Pseudomonas aeruginosa) and Gram (+) (Staphylococcus aureus) bacteria of the obtained films were studied. From the morphological analysis, good emulsion stability and porosity were obtained in the Pickering films with the highest oil content, while instability was observed in the Pickering films with the lowest concentration of oil content. Thermal and spectroscopic analysis indicated there was no significant difference between the Pickering emulsion films and neat films. With the addition of Pickering emulsions, the tensile stress values decreased from 7.3 ± 1.9 MPa to 3.3 ± 0.2. According to the antibacterial efficiency results, films containing pumpkin powder and Pickering emulsion films containing both pumpkin powder and a ratio of 1:1 (β-CD/NEO) did not have an antibacterial effect, while Pickering emulsion films with a ratio of (β-CD/NEO) 1:3 and 1:5 showed an antibacterial effect against Escherichia coli, with a zone diameter of 12 cm and 17 cm, respectively. Among the samples, the films with ratio of (β-CD/NEO) 1:5 had the highest antioxidant capacity, as assessed by DPPH radical scavenging at 12 h intervals. Further, none of the samples showed any cytotoxic effects the according to LDH and WST-1 cytotoxicity analysis for the NIH3T3 cell line. Ultimately, it is expected that these films are completely bio-based and may be potential candidates for use in wound healing applications.

In this study, polyvinyl alcohol (PVA) and psyllium husk (PSH)/D-limonene electrospun meshes were produced by emulsion electrospinning for use as substrates to prevent the growth of bacteria. D-limonene and modified microcrystalline cellulose (mMCC) were preferred as antibacterial agents. SEM micrographs showed that PVA–PSH electrospun mesh with a 4% amount of D-limonene has the best average fiber distribution with 298.38 ± 62.8 nm. Moreover, the fiber morphology disrupts with the addition of 6% D-limonene. FT-IR spectroscopy was used to analyze the chemical structure between matrix–antibacterial agents (mMCC and D-limonene). Although there were some partial physical interactions in the FT-IR spectrum, no chemical reactions were seen between the matrixes and the antibacterial agents. The thermal properties of the meshes were determined using thermal gravimetric analysis (TGA). The thermal stability of the samples increased with the addition of mMCC. Further, the PVA–PSH–mMCC mesh had the highest value of contact angle (81° ± 4.05). The antibacterial activity of functional meshes against Gram (−) (Escherichia coli, Pseudomonas aeruginosa) and Gram (+) bacteria (Staphylococcus aureus) was specified based on a zone inhibition test. PPMD6 meshes had the highest antibacterial results with 21 mm, 16 mm, and 15 mm against Escherichia coli, Staphylococcus aureus, and Pseudomonas aeruginosa, respectively. While increasing the amount of D-limonene enhanced the antibacterial activity, it significantly decreased the amount of release in cases of excess D-limonene amount. Due to good fiber morphology, the highest D-limonene release value (83.1%) was observed in PPMD4 functional meshes. The developed functional meshes can be utilized as wound dressing material based on our data.

In this study, the lavender essential oil-incorporated polylactic acid (PLA) nanofibers were fabricated by the electrospinning technique with the presence of kolliphor as a nonionic surfactant. The FTIR spectra supported the chemical composition of the fibers. The FTIR spectra demonstrated that there is no chemical reaction present between PLA and lavender essential oil. The SEM images of all nanofibers showed bead-free morphology. ImageJ results showed that the average diameter of lavender oil-loaded fibers ranged between 121.6 ± 32 and 228.2 ± 53 nm. All lavender essential oil-incorporated nanofibers were hydrophobic with satisfactory thermal properties. Furthermore, the lavender essential oil-incorporated PLA nanofibrous mats exhibited good antioxidant activity. The results showed that as the concentration of the essential oil in resulting nanofibers increased, the antioxidant activity also increased. According to the results of this study, lavender essential oil-loaded PLA fibers can be considered for a wide range of potential applications such as active packaging, food coating, facial masks, and wound dressing.