We explore the use of a highly nonlinear chalcogenide-silica waveguide for supercontinuum generation in the near infrared. The structure was fabricated by a pressure-assisted melt-filling of a silica capillary fiber (1.6 µm bore diameter) with Ga₄Ge₂₁Sb₁₀S₆₅ glass. It was designed to have zero group velocity dispersion (for HE₁₁ core mode) at 1550 nm. Pumping a 1 cm length with 60 fs pulses from an erbium-doped fiber laser results in the generation of octave-spanning supercontinuum light for pulse energies of only 60 pJ. Good agreement is obtained between the experimental results and theoretical predictions based on numerical solutions of the generalized nonlinear Schrödinger equation. The pressure-assisted melt-filling approach makes it possible to realize highly nonlinear devices with unusual combinations of materials. For example, we show numerically that a 1 cm long As₂S₃:silica step-index fiber with a core diameter of 1 µm, pumped by 60 fs pulses at 1550 nm, would generate a broadband supercontinuum out to 4 µm.

We report a hybrid chalcogenide–silica photonic crystal fiber made by pressure-assisted melt-filling of molten glass. Photonic bandgap guidance is obtained at a silica core placed centrally in a hexagonal array of continuous centimeters-long chalcogenide strands with diameters of $1.45\mathrm{\mu m}$. In the passbands of the cladding, when the transmission through the silica core is very weak, the chalcogenide strands light up with distinct modal patterns corresponding to Mie resonances. In the spectral regions between these passbands, strong bandgap guidance is observed, where the silica core transmission loss is $60\mathrm{dB}/\mathrm{cm}$ lower. The pressure-assisted fabrication approach opens up new ways of integrating sophisticated glass-based devices into optical fiber circuitry with potential applications in supercontinuum generation, magneto-optics, wavelength selective devices, and rare-earth-doped amplifiers with high gain per unit length.