Variations on the processing conditions of conventional methods for polymeric film preparation may allow tuning certain properties. In this work, different casting surfaces and humidity are presented as variables to consider for cellulose acetate (CA) film preparation using conventional solution casting method. Specifically, borosilicate glass, soda-lime glass and Teflon (PTFE) dishes have been used for casting and their influence on various properties on CA films assessed. The surfaces of glass dishes are smooth, while PTFE surface has a pattern constituted by concentric channels of micro dimensions (as seen by optical microscope), which is adopted by cast films upon drying. The resulting patterned films are translucent while films produced using smooth surfaces are transparent. The effect of the environment humidity (35%, 55% and 75% RH) in the properties of the CA films during the evaporation of solvent from solution has been evaluated. Higher humidity produces smoother surfaces and increased crystallinity as shown by XRD and DSC; however, the wettability of the films does not seem to be influenced by this variable. Due to the specific morphology of the patterned films, changes in material opacity upon wetting are detected, from translucent to transparent, while the removal of water from the surface restores the translucency. This micropatterning effect that causes different visual appearance of the material can find use as a humidity sensor in food packaging applications.

In the past two decades, a growing body of research regarding the utilization of natural bacterial pigments or dyes for textile dyeing has emerged. Bacterial pigments are bacterial secondary metabolites that usually have bright colors and some special properties (e.g., antimicrobial, antioxidative, UV protective etc.). In addition to their high production yield, these special properties led scientists to research and develop methods for utilizing bacterial pigments in textile dyeing. This study presents the current state this field of research, with a focus on the dyeing potential of bacterial pigments for different types of textile material. The potential future directions of research in this area are also highlighted. In addition to the durable dyeing of textiles, bacterial pigments with special properties, such as antimicrobial activity, can add multifunctionality to dyed materials, thus increasing the value of the final product. This emerging field of research will also have a great impact on sustainability and the environment, contributing to the decreased usage of synthetic dyes in the textile industry.

In the past decades, cellulose (one of the most important natural polymers), in the form of nanofibers, has received special attention. The nanofibrous morphology may provide exceptional properties to materials due to the high aspect ratio and dimensions in the nanometer range of the nanofibers. The first feature may lead to important consequences in mechanical behavior if there exists a particular orientation of fibers. On the other hand, nano-sizes provide a high surface-to-volume ratio, which can have important consequences on many properties, such as the wettability. There are two basic approaches for cellulose nanofibers preparation. The top-down approach implies the isolation/extraction of cellulose nanofibrils (CNFs) and nanocrystals (CNCs) from a variety of natural resources, whereby dimensions of isolates are limited by the source of cellulose and extraction procedures. The bottom-up approach can be considered in this context as the production of nanofibers using various spinning techniques, resulting in nonwoven mats or filaments. During the spinning, depending on the method and processing conditions, good control of the resulting nanofibers dimensions and, consequently, the properties of the produced materials, is possible. Pulp, cotton, and already isolated CNFs/CNCs may be used as precursors for spinning, alongside cellulose derivatives, namely esters and ethers. This review focuses on various spinning techniques to produce submicrometric fibers comprised of cellulose and cellulose derivatives. The spinning of cellulose requires the preparation of spinning solutions; therefore, an overview of various solvents is presented showing their influence on spinnability and resulting properties of nanofibers. In addition, it is shown how bottom-up spinning techniques can be used for recycling cellulose waste into new materials with added value. The application of produced cellulose fibers in various fields is also highlighted, ranging from drug delivery systems, high-strength nonwovens and filaments, filtration membranes, to biomedical scaffolds.