This work reports on determination of the influence of passivation type of Ti15wt.%Mo implant alloy surface on its corrosion resistance in simulated body fluids. The alloy under investigation was subjected to natural self-passivation in air, and forced passivation by autoclaving in steam, boiling in 30 % solution of H2O2, and electrochemical passivation in 0.9 % NaCl solution. Resistance of the passivated Ti15Mo alloy to pitting corrosion was studied at 37ºC in 0.9 % NaCl solution using open circuit potential method, anodic polarization curves, and electrochemical impedance spectroscopy (EIS). Comparative estimation of the determined parameters of corrosion resistance revealed that the obtained passive layers improve anticorrosive properties of the tested alloy. Surface of the alloy subjected to passivation in steam autoclave reveals the highest protection against pitting corrosion. Anodic potentiodynamic curves showed that the Ti15Mo alloy after different passivation types of the surface is characterized by a lack of susceptibility to pitting corrosion up to potential of 9 V. Based on the EIS investigations, the thickness of the formed oxide layers (TiO2, anatase) was determined to be in the range from 2.0 to 7.8 nm in dependence on the applied type of passivation. It was ascertained that electrochemical properties of the Ti15Mo alloy and possibility of its surface passivation using simple methods, make it an attractive material for use in biomedicine for long-term implants

The presented work was focused on investigating the influence of the (hafnium and zirconium)/molybdenum ratio on the microstructure and properties of Ti₂₀Ta₂₀Nb₂₀(ZrHf)_20−xMo_x (where: x = 0, 5, 10, 15, 20 at.%) high entropy alloys in an as-cast state. The designed chemical composition was chosen due to possible future biomedical applications. Materials were obtained from elemental powders by vacuum arc melting technique. Phase analysis revealed the presence of dual body-centered cubic phases. X-ray diffraction showed the decrease of lattice parameters of both phases with increasing molybdenum concentration up to 10% of molybdenum and further increase of lattice parameters. The presence of two-phase matrix microstructure and hafnium and zirconium precipitates was proved by scanning and transmission electron microscopy observation. Mechanical property measurements revealed decreased micro- and nanohardness and reduced Young’s modulus up to 10% of Mo content, and further increased up to 20% of molybdenum addition. Additionally, corrosion resistance measurements in Ringers’ solution confirmed the high biomedical ability of studied alloys due to the presence of stable oxide layers.

Chitosan biocoatings were successfully deposited on the Ti15Mo alloy surface via cataphoretic deposition from a solution of 1 g dm⁻³ of chitosan in 4% (aq) citric acid.