This article deals with the dissimilar joining of two different grade Cr-Mo steel (2.25Cr-1Mo: P22 and modified 9Cr-1Mo: P91) for power plant application. The dissimilar butt-welded joint was produced for conventional V groove design by using the gas tungsten arc welding (GTAW) process with the application of an ERNiCrMo-3 Ni-based super alloy filler. A microstructure characterization was performed to measure the inhomogeneity in the microstructure and element diffusion across the interface in a welded joint. The experiments were also performed to evaluate the mechanical properties of the dissimilar welded joint in as-welded (AW) and post-weld heat treatment (PWHT) conditions. An acceptable level of the mechanical properties was obtained for the AW joint. After PWHT, a significant level of the element diffusion across the interface of the weld metal and P22 steel was observed, resulting in heterogeneity in microstructure near the interface, which was also supported by the hardness variation. Inhomogeneity in mechanical properties (impact strength and hardness) was measured across the weldments for the AW joint and was reduced after the PWHT. The tensile test results indicate an acceptable level of tensile properties for the welded joint in both AW and PWHT conditions and failure was noticed in the weak region of the P22 steel instead of the weld metal.

A dissimilar welded joint of Inconel 718 and 304L austenitic stainless steel was prepared using a combined procedure with the gas tungsten arc welding and shielded metal arc welding processes by employing the Ni-based fillers: ERNiCr-3 and ENiCrFe-3. The welded joints were investigated for metallographic testing and mechanical properties, and a relationship was established between the microstructure and the resultant mechanical properties. Microstructural observation revealed the formation of the unmixed zone on the 304L SS side. The weld metal showed that the fully austenitic microstructure consisted of the Nb- and Ti-rich carbide phases along the inter-dendritic spaces. The tensile test results at room temperature showed the failure from the weld metal which might be due to alloying element segregation along the inter-dendritic spaces. However, a tensile test at 600 °C showed the failure from the 304L SS base metal with a tensile strength and % elongation value of 377 MPa and 24%, respectively. The hardness plot showed the average hardness value of the weld metal of 236 ± 5 HV, which was higher than the 304L SS BM (204 ± 4 HV) but lower than the IN718 BM (243 ± 5 HV). The impact toughness of the weld metal was 109 J, which was significantly lower than the base metals. The poor impact strength of the weld metal might be due to the evolution of the NbC phase along inter-dendritic spaces.

The objective of the current study was to analyse the microstructure, mechanical characteristics, and residual stresses of a dissimilar welded joint (DWJ) made of P92 steel and the Inconel alloy 617 (IN617) using the gas tungsten arc welding (GTAW) method. The ERNiCr-3 filler was selected to produce the conventional V groove (VG) and narrow V groove (NVG) butt joint. The filler deficient zones in the weldments, such as the filler deficient beach, i.e. unmixed zone (UZ), peninsula, and island, as well as the distinct heat-affected zone (HAZ), were visible near the interface of ERNiCr-3 filler weld and P92 steel due to the distinct differences in the chemical composition, microstructure, and mechanical properties between the filler and P92 base metal (BM). A very narrow partial melted zone (PMZ) and almost negligible UZ and HAZ were noticed at the interface of IN617 and ERNiCr-3 weld metal and it occurred mainly due to the similarity in microstructure and melting point. The austenitic microstructure of ERNiCr-3 filler weld was accompanied by precipitates enriched with Ti and Nb along with the inter-dendritic space. At room temperature, the mechanical properties of both the groove joints were evaluated, and the test results indicated that the welded joint satisfied the standard requirements for AUSC power plants' boiler applications. The tensile test results showed the failure from ERNiCr-3 filler weld with a tensile strength of 627 ± 2 MPa and 636 ± 3 MPa for VG and NVG welded joints, respectively. A poor weld metal impact toughness in comparison to the BMs was attributed to the presence of the brittle Ti(C, N) and Nb(C) particles in the interdendritic space. The impact toughness for the NVG weld joint was measured higher than for the VG weld joint. A significant hardness deviation was measured along the weldments that might be due to heterogeneous microstructure, i.e. UZ, HAZ, delta ferrite, and weld metal. To impart the ductility and temper the martensite in P92 HAZ, post-weld heat treatment (PWHT) was also performed, and a studied their effect on microstructure evolution across the weldments and mechanical properties. Groove design also showed a significant effect on residual stress variation. The work highlights the groove geometry, welding procedure, evolution of the microstructure along the weldments, mechanical characteristics, and residual stress variation of DWJ of P92 steel and IN617 alloy. In comparison to conventional VG joints, the NVG joints exhibited superior mechanical properties and lower residual stress values.

The 9% Cr steels were developed for ultra-supercritical (USC) power plants to meet the requirements of high operating temperature and pressure. These steels are produced to operate at high temperatures where impact toughness is not a concern; however, it becomes important for the welded joints to have good impact toughness at room temperature for manufacturing. The present work investigates the effect of the post-weld heat treatment (PWHT) parameters, i.e., temperature and time, on the impact toughness of multi-pass gas tungsten arc welded (GTAW) joints of ferritic/martensitic grade P92 steel. The microstructural evolution in welded joints given varying post-weld temperatures and times was studied. The lath martensitic structure of the weld metal for the as-welded joints resulted in high hardness and low impact toughness. The weld fusion zone toughness was 12 J, which was lower than the minimum specified values of 41 J (ASME standards) and 47 J (EN ISO 3580:2017). The PWHT temperature and time were found to have a significant effect on the impact toughness of the weld metal. A drastic increase in the impact toughness of the weld metal was noticed, which was attributed to lath break-up, reduction in dislocation density and reduction in solid solution hardening. The maximum impact toughness of 124 J was measured for PWHT temperature and time of 760 °C and 120 min, respectively. The effect of PWHT parameters on tensile strength was also investigated, and test results showed that the joint was safe for USC boiler application as it failed from the region of the P92 base metal. The variation in microstructural evolution along the weldments resulted in hardness variation. PWHT led to homogeneity in microstructure and, ultimately, reduction in hardness value. According to the study, the optimum temperature and time for PWHT of a GTAW joint of P92 steel were found to be 760 °C and 120 min, respectively.

Restrictive operating conditions (even exceeding 700 °C) of materials in advanced ultra super critical (AUSC) power plants and the need to minimize manufacturing and maintenance costs require the production of dissimilar metal welded joints (DMW). Significant differences in the physical and chemical properties of welded materials lead to phenomena that reduce the weldability of the metals used and force the search for solutions that limit unfavorable phenomena, e.g., the use of buttering layers. The study presents a comparison of two types of joints with Alloy 617 (UNS N06617) and ferritic P92 (UNS K92460) steel made using Inconel 82 (ENiCrFe-3) and Inconel 617 (ERNiCrCoMo-1) alloys buttering layer and the corresponding chemical composition of filler metals. All areas of the joints made with the gas tungsten arc welding process were subjected to structural investigations (optical microscopy, scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDS) and mechanical tests (microhardness, room and high temperature tensile, and toughness testing). Despite the more complicated welding procedure, sound welded joints were obtained with favorable properties resulting, inter alia, from the reduced thickness of the martensite layer in HAZ of P92 steel and the limited diffusion of alloy components compared to welded joints without the buttering layer. This also resulted in a reduction of the maximum hardness (especially in the case of Inconel 82 buttering—by 15–30 HV0.5 in comparison with Inconel 617 buttering) and an increase in strength while limiting the decrease in plasticity (even 663 MPa tensile strength and 21% of elongation for Inconel 617 buttered joint). Moreover, improved high-temperature performance (approximately 70–100 MPa) of the welded joint following the application of the buttering layer was confirmed. The presented results allow for drawing general conclusions that both proposed welding procedures can be recommended for use in the working conditions occurring at AUSC.