In this work, grapheme oxide (GO) nano-sheets were synthesized and dispersed in the aqueous phase for the interfacial polymerization (IP) process to develop a new type of thin-film composite (TFC) membranes for forward osmosis (FO) applications. The effects of the GO concentrations on the membrane surfaces and cross-sectional morphologies and FO desalination performances of the as-prepared TFC membranes were investigated systematically. Compared with the control membrane, the optimal GO-incorporated TFC membrane displayed higher water flux, less specific reverse solute flux (SRSF) and lower structure parameter. Moreover, the optimized membrane showed 75.0 times higher chlorine resistance than the control membrane. In general, these new type of membranes could be an effective strategy to fabricate high-performance FO membranes with good desalination performance and chlorine resistance.

The Forward Osmosis (FO) membrane was the core of FO technology. Obtaining a high water flux while maintaining a low reverse solute flux has historically been considered the gold standard for a perfect FO membrane. In a thin-film composite FO membrane, the performance of the membrane was determined not only by the material and structure of the porous support layer but also by the structural and chemical properties of the active selective layer. Researchers have selected numerous sorts of materials for the FO membranes in recent years and have produced exceptional achievements. Herein, the performance of the modified FO membrane constructed by introducing new two-dimensional nanomaterial MXene nano-sheets to the interfacial polymerization process was investigated, and the performance of these modified membranes was investigated using a variety of characterization and testing methods. The results revealed that the MXene nano-sheets played an important role in improving the performance of the FO membrane. Because of the hydrophilic features of the MXene nano-sheets, the membrane structure may be tuned within a specific concentration range, and the performance of the modified FO membrane has been significantly enhanced accordingly. The optimal membrane water flux was boosted by around 80%, while its reverse solute flux was kept to a minimum of the resultant membranes. It showed that the addition of MXene nanosheets to the active selective layer could improve the performance of the FO membrane, and this method showed promising application prospects.