The microstructure and strength characteristics of the Ti–6Al–4V alloy prepared using the selective laser melting (SLM) method with different sample building geometry using an EOSINT M280...

The process of an unstable plastic flow associated with the strain rate sensitivity of mechanical properties was studied in porous 316L austenitic steel samples manufactured by laser powder bed fusion (L-PBF). Different micromechanisms of deformation and fracture of porous samples dependent on strain rate were found. It was found that despite the porosity, the specimens showed high strength, which increased with the loading rate. Porosity led to lower ductility of the studied specimens, in comparison with literature data for low porous 316L L-PBF samples and resulted in de-localization of plastic deformation. With an increase in strain rate, nucleation of new pores was less pronounced, so that at the highest strain rate of 8 × 10⁻³ s⁻¹, only pore coalescence was observed as the dominating microscopic mechanism of ductile fracture.

Laser shock peening (LSP) is a relatively novel and promising surface hardening method. An absorbing layer, which is needed to protect the specimen surface from undesirable thermal effects caused by laser irradiation, should be considered as one of many varying parameters. The physical characteristics of the coating and its adhesion to the specimen surface can significantly influence the result of LSP. In this study, three commonly used absorbing coatings, namely black polyvinylchloride tape with a sticky layer, aluminum foil, and black alkyd paint were used to cover three-millimeter-thick plates of the Ti-6Al-4V titanium alloy with globular or lamellar microstructures. LSP of one side of the plates was carried out with a power density of 10 GW/cm². The hole drilling method was used to evaluate residual stresses. The aluminum foil was found to be the optimal option for LSP of the Ti-6Al-4V titanium alloy. Microstructural investigations carried out using EBSD analysis suggested that no significant reduction in grain size, twinning, or dislocation density growth occurred as a result of LSP irrespective of the initial structure.