Erosive beverages cause dissolution of natural teeth and intra-oral restorations, resulting in surface characteristic changes, particularly roughness and degradation. The purpose of this study was to evaluate the surface roughness and topography of a dental ceramic following immersion in locally available erosive solutions. A total of 160 disc specimens of a nano-fluorapatite type ceramic (12 mm diameter and 2 mm thickness) were fabricated and equally distributed into two groups (n = 80) and then evenly distributed among the following five testing groups (n = 16): lemon juice, citrate buffer solution, 4% acetic acid, soft cola drink, and distilled water which served as a control. The surface roughness (Ra) and topography were evaluated using a profilometer and scanning electron microscope at baseline, 24 h, 96 h, and 168 h respectively. Data were analyzed using ANOVA and Tukey’s multiple comparisons (p ≤ 0.05). Surface changes were observed upon exposure to all acidic beverages except distilled water. Amongst all immersion media, 4% acetic acid produced the most severe surface roughness across all time periods (i.e., baseline, 24 h, 96 h, and 168 h). A statistically significant difference in the surface roughness values between all immersion media and across all four time intervals was observed. Erosive agents had a negative effect on the surface roughness and topography of the tested ceramic. The surface roughness increased with increased storage time intervals.

Background: This study aimed to observe the impact of service learning on the attitude of senior dental students toward community service.Methods: A cross-sectional survey-based was conducted and recruited a total of 120 senior students of Dentistry Taibah University that were enrolled in a clinical service-learning course using convenience sampling. The attitude of dental college students toward community service based on the model of helping behavior by Schwartz was evaluated through Community Service Attitude Scale (CSAS). The data was collected using the same questionnairesfor the pre-test and post-test. Data were analyzed by using SPSS 25. A repeated-measures mixed-model ANOVA was used to test the changes across pre-and post-test.Results: A total of 96 students completed the first survey, making a response rate of 80%, and 78 among them completed the second survey as well, making a response rate of 81%. Significant change (P < 0.0001) in ANOVA indicated that there was an overall change in attitude. Conclusions: It can be concluded that community-based service-learning positively impacts the attitude of last year’s dental students toward understanding needs at the community level and the attitude to help in providing dental care at the community level.

The essential factor in determining the preservation of restoration is the marginal seal. Restoring cervical lesions with a resin composite has always been a challenge. Composite resins with various viscosities and different bonding systems are being researched to reduce the microleakage. Confocal laser scanning microscopy (CLSM) is the latest non-destructive technique for visualizing the microleakage. Objectives: To evaluate and compare the microleakage of Universal Flo composite resin (G-aenial) using etch and rinse adhesive system ER-2 steps (Adper Single Bond 2), self-etch adhesive system SE-1 step (G-Bond), and self-adhesive flowable composite resin (Constic) in Class V cavities using a confocal laser scanning microscope. Materials and Method: Class V cavities were prepared on 27 caries-free human extracted premolar teeth on the buccal and lingual surfaces with standardized dimensions of 2 mm height, width 4 mm, and a depth of 2 mm. After the cavity preparation, all teeth were randomly divided into three groups, namely Group-I: G-aenial Universal Flo with Single Bond 2 (n = 9 teeth); Group-II: G- aenial Universal Flo with G-Bond (n = 9 teeth), and Group-III: Constic (n = 9 teeth). The prepared and restored specimens were then subjected to thermocycling for 500 cycles in a water bath at 5 °C and 55 °C with a dwelling time of 30 s. The specimens were placed in 0.6% aqueous rhodamine dye for 48 h. Sectioning was carried out bucco-lingually and specimens were evaluated for microleakage under a confocal laser scanning microscope. Results: There was a significant difference (p = 0.009) in microleakage when comparing total etch and rinse, specifically between Adper Single Bond 2 ER-2 steps (fifth generation) and self-adhesive flowable composite resin, which is Constic. There was more microleakage in the self-etch bonding agent, particularly G-Bond, SE-1 step (seventh generation), when compared to ER-2 steps (fifth generation bonding agent); however, the results were not statistically significant (p = 0.468). The self-adhesive flowable composite resin showed more microleakage than SE-1 step and ER-2 steps. Conclusions: None of the adhesive systems tested were free from microleakage. However, less microleakage was observed in the total etch and rinse, especially Adper Single Bond 2 (ER-2 steps), than the self-etch adhesive system SE-1 step and self-adhesive flowable composite resin. Clinical significance: Constant research and technological advancements are taking place in dentin adhesives to improve the marginal seal. This has led to the evolution of total acid-etching dentin bonding agents termed as etch and rinse (ER)-2 steps (fifth generation dentin bonding agents) and self-etching (SE) 2 steps, and SE-1 step dentin bonding agents termed as the sixth and seventh generation bonding agents, respectively.

Endodontic technical errors are the foremost cause of treatment failure. A thorough understanding of root canal configuration (RCC) is essential to prevent these iatrogenic errors. This study used CBCT images to determine the association between root canal configuration, endodontic technical errors, and periapical status. CBCT images of 101 patients, including total of 212 obturated premolars (256 canals) were assessed. RCCs were classified according to the Vertucci system. The presence of endodontic errors and periapical lesions associated with each RCC was noted. Presence or absence of coronal restoration and its association with periapical radiolucency was recorded. The most frequent RCC was Type I (199 cases; 77.73%), followed by Type II (26 cases; 10.15%), Type IV (22 cases; 8.59%), Type V (4 cases; 1.56%), Type III (4 cases; 1.56%), and Type VI (1 case; 0.39%). Under-filling and non-homogeneous filling were the most common technical errors. Prevalence of periapical radiolucency was 81% in the presence of technical errors. The absence of coronal restoration caused apical lesions in 93% of cases. The frequency of endodontic technical errors increased as the root canal configurations became more complex. Periapical lesions occurred more often in teeth with endodontic errors and/or absent coronal restoration.

Dental pulp treatment is the least intrusive procedure currently available for preserving the vitality of the pulp. Several studies are underway to improve the bioactivity of pulp capping materials. Tideglusib isa potent anti-inflammatory, antioxidant, and a regenerative drug developed against Alzheimer’s disease and has been shown to be effective in the treatment of dental cavities. However, its bioactive properties encapsulated within the nanoparticles as a component of pulp capping material are largely unknown. In this study, tideglusib-loaded bioactive glass nanoparticles were synthesized (tideglusib-BgNPs) and mixed at various concentrations into the calcium silicate cement to testits physiomechanical and bioactivitiescompared with biodentine (control). The calcium silicate cement with 10wgt% tideglusib-BgNPs showed comparable physiomechanical properties to that of biodentine. Additionally, the assessment of cytotoxicity and bioactivity (cell proliferation, wound healing, and cell migration assays) showed increased bioactivity in terms of better wound healing, increased proliferation, and better migration of human dental pulp stem cells than biodentine. These findings suggest new opportunities to use tideglusib-BgNPs in pulp therapy.

Objective To explore perceptions of undergraduate dental students regarding difficulties faced during endodontic procedures. Methods An e-questionnaire was sent to 57 fourth-year and 45 fifth-year dental students. It comprised questions regarding demographic data and difficulties faced during different steps of the endodontic treatment. The responses were recorded on a 5-point Likert scale. During dichotomization, responses where one and two were chosen were considered yes whereas responses where three, four, and five were chosen were considered no. The sample size (SS) calculated using the Qualtrics SS calculator was 89. Data were analyzed using SPSS version 20. Frequencies and percentages were calculated. A p-value of less than 0.05 was considered significant. The chi-square test was applied for comparison based on the students’ academic year and genders. Results Ninety students responded with an 88.2% response rate. Most students reported not facing any difficulty in differentiating healthy pulp and periapex from conditions of pulp pathosis (78.9%) and periapical pathosis (75.6%). Most males found access opening and de-roofing of the pulp chamber (35.6%) and working length determination (31.1%) difficult. Females reported having difficulty mostly in mesial and distal shift radiograph techniques (55.6%) and access openings (51.1%). No statistical difference was found based on an academic year or gender except in the use of mesial and distal shift techniques for radiograph acquisition Conclusion Assessing difficulties encountered by students during endodontic therapy can aid in the development of teaching strategies for preclinical and clinical instruction. Mesial and distal shift techniques, access cavity preparation, and working length determination are areas requiring more focus in the training process.