This work describes the development of a new process for the recovery of Li, Al and Si along with the proposal of a flow sheet for the precipitation of those metals. The developed process is comprised of lepidolite acid digestion with hydrofluoric acid, and the subsequent precipitation of the metals present in the leach liquor. The leaching operational parameters studied were: reaction time, temperature and HF concentration. The experimental results indicate that the optimal conditions to achieve a Li extraction higher than 90% were: solid-liquid ratio, 1.82% (w/v); temperature, 123 °C; HF concentration, 7% (v/v); stirring speed, 330 rpm; and reaction time, 120 min. Al and Si can be recovered as Na3AlF6 and K2SiF6. LiF was separated from the leach liquor during water evaporation, with recovery values of 92%.

Lithium (Li) is considered a strategic element whose use has significantly expanded. Its current high demand is due to its use in lithium ion batteries for portable electronic devices, whose manufacture and market are extensively growing every day. These days there is a great concern about the final disposal of these batteries. Therefore, the possibility of developing new methodologies to recycle their components is of great importance, both commercially and environmentally. This paper presents results regarding important operational variables for the dissolution of the lithium and cobalt mixed-oxide (LiCoO₂) cathodes from spent lithium ion batteries (LIBs) with hydrofluoric acid. The recovery and synthesis of Co and Li compounds were also investigated. The dissolution parameters studied were: temperature, reaction time, solid-liquid ratio, stirring speed, and concentration of HF. The investigated recovery parameters included: pH, temperature, and time with and without stirring. The final precipitation of lithium fluoride was also examined. The results indicate that an increase in the HF concentration, temperature, and reaction time favors the leaching reaction of the LiCoO₂. Dissolutions were close to 60%, at 75 °C and 120 min with a HF concentration of 25% (v/v). The recovery of Co and Li were 98% and 80%, respectively, with purities higher than 94%. Co and Li compounds, such as Co₃O₄ and LiF, were synthesized. Furthermore, it was possible to almost completely eliminate the F⁻ ions as CaF₂.

In this work, a recycling route for spent Li-ion batteries (LIBs) was developed. For this, the recovery of the metal content in both electrodes (anode and cathode) was investigated. Based on these results, an economic analysis of this recycling process was carried out. The obtained results showed that more than 90% of the material contained in both electrodes was recycled. The dissolution with acetic acid of the metals present in the active cathodic material is thermodynamically viable and the addition of a reducing agent such as hydrogen peroxide improved the spontaneity of the reaction. Dissolutions close to 100% for Li and Co were obtained. In addition, it was determined that the synthesis of lithium and cobalt valuable compounds was viable from the leach liquor, recovering approximately 90% of Co as cobalt oxalate, and 92% of Li as lithium carbonate. Furthermore, carbon graphite and Cu were fully recovered (100%) from the anodes. Finally, the results of the economic analysis showed that the recovered products have a high commercial value and industrial interest, providing an environmentally and economically viable process.