The fabrication of a ZnO/Au nanosquare-array electrode was successfully carried out for the detection of glucose concentration in biomedical applications. The fabrication of the ZnO/Au nanosquare array using an ultra-thin alumina mask (UTAM) based on the imprinted anodic aluminum oxide (AAO) template and the direct current (DC) sputtering method was able to produce a very well-ordered nanosquare arrangement with a side size of 300 nm and a thickness of 100 nm. Tests were done to evaluate the performance of the electrode by means of cyclic voltammetry (CV) which showed that the addition of glucose oxidase (GOx) increased the sensitivity of the electrode up to 1180 ± 116 μA mM⁻¹cm⁻², compared with its sensitivity prior to the addition of GOx of 188.34 ± 18.70 mA mM⁻¹ cm⁻². A i_ox/i_red ratio equal to ~1 between the peaks of redox reactions was obtained for high (hyperglycemia), normal, and low (hypoglycemia) levels of glucose. The ZnO/Au nanosquare-array electrode was 7.54% more sensitive than the ZnO/Au thin-film electrode. Furthermore, finite-difference time-domain (FDTD) simulations and theoretical calculations of the energy density of the electric and magnetic fields produced by the ZnO/Au electrode were carried out and compared to the results of CV. From the results of CV, FDTD simulation, and theoretical calculations, it was confirmed that the ZnO/Au nanosquare array possessed a significant optical absorption and that the quantum effect from the nanosquare array resulted in a higher sensitivity than the thin film.

The development of silver (Ag) thin films and the fabrication of Ag nanosquare arrays with the use of an anodic aluminum oxide (AAO) template and leaf extracts were successfully carried out using the DC sputtering and spin coating deposition methods. Ag thin films and Ag nanosquare arrays are developed to monitor cancer prognosis due to the correlation between serum albumin levels and prognostic factors, as well as the binding of serum albumin to the surface of these electrodes. Nanosquare structures were fabricated using AAO templates with varying diameters and a gap distance between adjacent unit cells of 100 nm. The nanosquare array with a diameter of 250 nm and irradiated with electromagnetic waves with a wavelength of around 800 nm possessed the greatest electric field distribution compared to the other variations of diameters and wavelengths. The results of the absorption measurement and simulation showed a greater shift in absorption peak wavelength when carried out using the Ag nanosquare array. The absorption peak wavelengths of the Ag nanosquare array in normal blood and blood with cancer lymphocytes were 700–774 nm and 800–850 nm, respectively. The electrochemical test showed that the sensitivity values of the Ag thin-film electrode deposited using DC sputtering, the Ag thin-film electrode deposited using spin coating, and the Ag nanosquare array in detecting PBS+BSA concentration in the cyclic voltammetry (CV) experiment were 1.308 µA mM⁻¹cm⁻², 0.022 µA mM⁻¹cm⁻², and 39.917 µA mM⁻¹cm⁻², respectively. Meanwhile, the sensitivity values of the Ag thin film and the Ag nanosquare array in detecting the PBS+BSA concentration in the electrochemical impedance spectroscopy (EIS) measurement were 6593.76 Ohm·cm²/mM and 69,000 Ohm·cm²/mM, respectively. Thus, our analysis of the optical and electrochemical characteristics of Ag thin films and Ag nanosquare arrays showed that both can be used as an alternative biomedical technology to monitor the prognosis of blood cancer based on the concentration of serum albumin in blood.

The fabrication of silver (Ag) and gold (Au) thin film electrodes was successfully carried out using the DC sputtering deposition method. These thin film electrodes were able to detect the increase in serum albumin concentration that was used as a prognostic factor for leukemia. The simulation and the optical experimental analysis show that an increase in BSA concentration can increase the absorbance peak observed at a wavelength of 435 nm on hypoalbumin medium and 470 nm on normal concentration of serum albumin medium. The performance of the electrodes was electrochemically tested, in which it was shown that a decrease in oxidation and reduction peaks occurred with respect to an increase in BSA concentration. An oxidation peak was observed at a voltage of 0.5 V for the Ag thin film. For the Au, Au/Ag, and Ag/Au thin films, an oxidation peak was observed at a voltage of 1.0 V. The limits of detection (LODs) of the Ag, Ag/Au, Au, and Au/Ag thin films were 0.56, 0.24, 0.64, and 0.36 g/dL, respectively. Therefore, based on both the electrochemical and optical analysis, the Ag/Au thin film possessed the highest potential for prognosis monitoring of leukemia compared with the other Ag and Au thin films.