An easily accessible photocathodic material was fabricated to realize high-efficiency water splitting. After optimizing the PEC system, the photocurrent was further amplified to −1.2 mA cm ⁻² .

Utilizing plasmonic nanostructures for efficient and flexible conversion of solar energy into electricity or fuel presents a new paradigm in photovoltaics and photoelectrochemistry research. In a conventional photoelectrochemical cell, consisting of a plasmonic structure in contact with a semiconductor, the type of photoelectrochemical reaction is determined by the band bending at the semiconductor/electrolyte interface. The nature of the reaction is thus hard to tune. Here instead of using a semiconductor, we employed a ferroelectric material, Pb(Zr,Ti)O₃ (PZT). By depositing gold nanoparticle arrays and PZT films on ITO substrates, and studying the photocurrent as well as the femtosecond transient absorbance in different configurations, we demonstrate an effective charge transfer between the nanoparticle array and PZT. Most importantly, we show that the photocurrent can be tuned by nearly an order of magnitude when changing the ferroelectric polarization in PZT, demonstrating a versatile and tunable system for energy harvesting.

Nanowire (NW) structures is an alternative candidate for constructing the next generation photoelectrochemical water splitting system, due to the outstanding optical and electrical properties. NW photoelectrodes comparing to traditional semiconductor photoelectrodes shows the comparatively shorter transfer distance of photo-induced carriers and the increase amount of the surface reaction sites, which is beneficial for lowering the recombination probability of charge carriers and improving their photoelectrochemical (PEC) performances. Here, we demonstrate for the first time that super-long Cu₂O NWs, more than 4.5 μm, with highly efficient water splitting performance, were synthesized using a cost-effective anodic alumina oxide (AAO) template method. In comparison with the photocathode with planar Cu₂O films, the photocathode with Cu₂O NWs demonstrates a significant enhancement in photocurrent, from –1.00 to –2.75 mA/cm² at –0.8 V versus Ag/AgCl. After optimization of the photoelectrochemical electrode through depositing Pt NPs with atomic layer deposition (ALD) technology on the Cu₂O NWs, the plateau of photocurrent has been enlarged to –7 mA/cm² with the external quantum yield up to 34% at 410 nm. This study suggests that the photoelectrode based on Cu₂O NWs is a hopeful system for establishing high-efficiency water splitting system under visible light.

The fabrication of a ZnO/Au nanosquare-array electrode was successfully carried out for the detection of glucose concentration in biomedical applications. The fabrication of the ZnO/Au nanosquare array using an ultra-thin alumina mask (UTAM) based on the imprinted anodic aluminum oxide (AAO) template and the direct current (DC) sputtering method was able to produce a very well-ordered nanosquare arrangement with a side size of 300 nm and a thickness of 100 nm. Tests were done to evaluate the performance of the electrode by means of cyclic voltammetry (CV) which showed that the addition of glucose oxidase (GOx) increased the sensitivity of the electrode up to 1180 ± 116 μA mM⁻¹cm⁻², compared with its sensitivity prior to the addition of GOx of 188.34 ± 18.70 mA mM⁻¹ cm⁻². A i_ox/i_red ratio equal to ~1 between the peaks of redox reactions was obtained for high (hyperglycemia), normal, and low (hypoglycemia) levels of glucose. The ZnO/Au nanosquare-array electrode was 7.54% more sensitive than the ZnO/Au thin-film electrode. Furthermore, finite-difference time-domain (FDTD) simulations and theoretical calculations of the energy density of the electric and magnetic fields produced by the ZnO/Au electrode were carried out and compared to the results of CV. From the results of CV, FDTD simulation, and theoretical calculations, it was confirmed that the ZnO/Au nanosquare array possessed a significant optical absorption and that the quantum effect from the nanosquare array resulted in a higher sensitivity than the thin film.

The fabrication of the photoanode of the n-type CuWO₄ nanorod arrays was successfully carried out through electrochemical deposition using anodic aluminum oxide (AAO) control templates and for the first time produced distinct gaps between the nanorod arrays. The effectiveness and efficiency of the resulting deposition was shown by the performance of the photoelectrochemical (PEC) procedure with a current density of 1.02 mA cm⁻² with irradiation using standard AM 1.5G solar simulator and electron changed radiation of 0.72% with a bias potential of 0.71 V (vs. Ag/AgCl). The gap between each nanorod indicated an optimization of the electrolyte penetration on the interface, which resulted in the expansion of the current density as much as 0.5 × 10²⁴ cm⁻³ with a flat band potential of 0.14 V vs. Ag/AgCl and also a peak quantum efficiency of wavelength 410 nm. Thus, also indicating the gaps between the nanorod arrays is a promising structure to optimize the performance of the PEC water splitting procedure as a sustainable energy source.