There have been numerous investigations regarding various types of dressings and artificial dermis of solid form, yet limited research and development on paste types, such as hydrogels with dermal powder, have ensued. In this study, we compared the in vivo wound healing effects of gelatin paste containing dermal powder to a collagen type I/chondroitin 6-sulfate (coll/chondroitin) sponge and gelatin alone, after 48 days post grafting, in a skin wound rat model. In the dermis powder/gelatin paste-treated group, wound area contraction was minimized 50%, while in the gelatin and coll/chondroitin sponge groups, the initial area contracted 83–85% and 79–85%, respectively. Histological analysis revealed the wounds treated with dermal powder/gelatin were associated with many fibroblasts, which infiltrated the wound bed, as well as thick collagen bundles that were arranged in dendritic arrays, resembling normal skin. Furthermore, in contrast to the gelatin- and coll/chondroitin sponge-treated groups, the powder/gelatin paste-treated wounds exhibited an abundance of elastic fibers (Victoria blue staining) and extensive formation of blood vessels around the dermis (CD31 staining). Therefore, the dermis powder/gelatin paste not only renders convenience to users but also has prominent wound-healing effects on full-thickness wounds.

Background: The aim of this study was to characterize the efficacy of nano-hydroxyapatite-coated silk fibroin constructs as a scaffold for bone tissue engineering and to determine the osteogenic effect of human dental pulp and periodontal ligament derived cells at an early stage of healing in rabbits. 3D silk fibroin constructs were developed and coated using nano-hydroxyapatite crystals. Dental pulp and periodontal ligament cells from extracted human third molars were cultured and seeded onto the silk scaffolds prior to in vivo implantation into 8 male New Zealand White rabbits. Four circular windows 8 mm in diameter were created in the calvarium of each animal. The defects were randomly allocated to the groups; (1) silk scaffold with dental pulp cells (DPSS), (2) silk scaffold with PDL cells (PDLSS), (3) normal saline-soaked silk scaffold (SS), and (4) empty control. The animals were sacrificed 2 (n = 4) or 4 weeks (n = 4) postoperatively. The characteristics of the silk scaffolds before and after cell seeding were analyzed using SEM. Samples were collected for histologic and histomorphometic analysis. ANOVA was used for statistical analysis. Result: Histologic view of the experimental sites showed well-maintained structure of the silk scaffolds mostly unresorbed at 4 weeks. The SEM observations after cell-seeding revealed attachment of the cells onto silk fibroin with production of extracellular matrix. New bone formation was observed in the 4 week groups occurring from the periphery of the defects and the silk fibers were closely integrated with the new bone. There was no significant difference in the amount of bone formation between the SS group and the DPSS and PDLSS groups. Conclusion: Within the limitations of this study, silk scaffold is a biocompatible material with potential expediency as an osteoconductive scaffold in bone tissue engineering. However, there was no evidence to suggest that the addition of hDPCs and hPDLCs to the current rabbit calvarial defect model can produce an early effect in augmenting osteogenesis.

In this study, silk thread (Bombyx mori) was braided to a tube-like shape and sericin was removed from the silk tube. Thereafter, collagen/chondroitin-6-sulfate solution was poured into the silk tube, and the lyophilization process was performed. To assess the inflammatory response in vivo, raw silk and sericin-free silk tubes were implanted in the subcutaneous layer of mice. After 10 days of in vivo implantation, mild inflammatory responses were observed around the sericin-free silk tubes, and severe inflammation with the presence of neutrophils and macrophages was observed around the raw silk tubes. At 24 weeks post implantation, the regenerated tendon had a thick, cylindrical, grayish fibrous structure and a shiny white appearance, similar to that of the native tendon in the rabbit model of tendon defect. The average tensile strength of the native tendons was 220 ± 20 N, whereas the average tensile strength of the regenerated tendons was 167 ± 30 N and the diameter of the regenerated tendon (3 ± 0.2 mm) was similar to that of the native tendons (4 ± 0.3 mm). Histologically, the regenerated tendon resembled the native tendon, and all the regenerated tissues showed organized bundles of crimped fibers. Masson trichrome staining was performed for detecting collagen synthesis, and it showed that the artificial tendon was replaced by new collagen fibers and extracellular matrix. However, the regenerated tendon showed fibrosis to a certain degree. In conclusion, the artificial tendon, comprising a braided silk tube and lyophilized collagen sponge, was optimal for tendon reconstruction. Thus, this study showed an improved regeneration of neo-tendon tissues, which have the structure and tensile strength of the native tendon, with the use of the combination of collagen and silk scaffold.

Melanin in the skin determines the skin color, and decreased melanin causes many hypopigmentation disorders and increased damage to skin by ultraviolet B (UVB) light irradiation. Here, we stimulate melanogenesis in B16F10 melanoma cells by using specific frequencies of ELF-EMFs. In this study, we focus on the melanogenesis of EMF-ELFs and find that 60-75Hz ELF-EMFs upregulate melanin synthesis by stimulated expression of tyrosinase and TRP-1 through inhibition of phosphorylation ERK, activation of CREB, and MITF up-regulation in B16F10 melanoma cells. The results show that 60-75Hz ELF-EMFs significantly increase secreted melanin, cellular melanin content, and tyrosinase activity, and the cell mitochondria activity, cell viability, and cell membrane condition are unchanged. Furthermore, the protein expression level of MITF and p-CREB signaling pathway are significantly increased. Moreover, 60Hz ELF-EMFs reduce the phosphorylate of ERK in B16F10 melanoma cells. These findings indicate that stimulation of melanogenesis by using ELF-EMFs has therapeutic potential for treating hypopigmentation disorders such as vitiligo.

The role of dental pulp stem cells (DPSCs) in dental tissue regeneration is gaining attention because DPSCs can differentiate into odontoblasts and other specialized cell types. Epigenetic modification has been found to play an important role in cell differentiation and regulation, among which histone deacetylase (HDAC) is involved in suppressing genes by removing histone acetyl groups. The use of HDAC inhibitor to control this is increasing and has been widely studied by many researchers. This study aimed to induce differentiation by causing epigenetic changes in odontoblast-related genes and the MAPK signaling pathway in human dental pulp stem cells. Western blot and immunofluorescence staining showed increased expression of DMP-1, ALP, DSPP, and RUNX2 compared to the control. However, activation of the MAPK signaling system was similar to but slightly different from the expression of odontoblast-related proteins. After 3 days, as shown by MTT and LDH assays, proliferation decreased overall, but cytotoxicity decreased at only a specific concentration. We confirmed that there was no change in mRNA expression of caspase 3 or 9 using real-time PCR. In addition, flow cytometry analysis confirmed that differentiation occurred due to the decrease in the expression of the CD73 and CD146. Although overall proliferation was reduced due to the G2/M inhibition of the cell cycle, the expression of BCL-2 protected the cells from cell death. Overall, cell proliferation decreased in response to MS-275, but it did not induce cytotoxicity in 5 nM and 10 nM concentration and induces differentiation into odontoblast-like cells.