Decreasing the clogging deposition rate of alumina inclusions in continuous casting nozzles is possible through three simultaneous measures: Flow modification, use of raw materials with low impurities contents, and smoothed internal surfaces. The control of the internal flow consists on avoiding dead regions and developing symmetric patterns. A mathematical model performed tests of the feasibility of these measures. The adherence of inclusions to the nozzle wall, using this model, employs a boundary condition based on the thickness of the sublaminar boundary instead of the conventional “trap” boundary condition. The use of the general boundary condition yields deposition rates that are unaffected by the inclusion size. The proposed boundary condition discriminates against the clogging deposition rate through the particle sizes. Plant trials complemented with water modeling, using these nozzles, proved that the present approach could considerably decrease the clogging occurrence.

Nozzle clogging in continuous casting of steel originates by the adherence of alumina particles and other oxides, precipitated during the liquid steel deoxidation, on the refractory material’s surface. Hence, these particles’ nucleation and growth rates in supersaturated melts are analyzed considering, specifically, the role of the interfacial tensions between alumina, silica, and other oxides and the liquid metal. Weak steel deoxidizers like silicon do not need high supersaturations favoring high nucleation rates, giving particles’ narrow size distributions thanks to fast diffusion and Ostwald-ripening coagulation. Strong deoxidizers, like aluminum, need high supersaturation levels leading to broad size distributions. Besides, the morphology of these particles depends on the nucleation and growth mechanisms. The adhesion forces among the deoxidation particles, forming clusters, depending on the morphology and the oxide’s chemistry. The stability of the nozzle’s clog, adhered to the nozzle’s wall, depends on the interface tensions between the melt and the nozzle’s refractory surface and between the melt and the inclusion. The results obtained here help set up basic recommendations in steel refining and materials specifications of casting nozzles.