The additive manufacturing (AM) technique can produce Ti-6Al-4V ELI (extra low interstitial) alloy for personalized biomedical devices. However, the Ti-6Al-4V ELI alloy presents poor tribological behavior. Regarding this, coatings are a feasible approach to improve the wear resistance of this alloy. In the literature, the tribological behavior of TiO₂ coatings incorporated with Ca and P formed by one-step plasma electrolytic oxidation (PEO) on Ti-6Al-4V ELI alloy processed by AM has not been investigated. Thus, in the present work, it was studied the influence of Ti-6Al-4V ELI alloy processed by AM on the wear resistance and morphologic of the coating obtained by PEO (plasma electrolytic oxidation). In this way, three different voltages (200, 250, and 300 V) were employed for the PEO process and the voltage effect on the properties of the coatings. The coatings were characterized by contact profilometry, scanning electron microscopy, energy-dispersive spectroscopy, the sessile drop method, grazing-incidence X-ray diffraction, and wear tests, on a ball-on-plate tribometer. The increase in applied voltage promoted an increase in roughness, pore area, and a decrease in the pore population of the coatings. In addition, the coatings, mainly composed of anatase and rutile, showed good adhesion to the metallic substrate, and the presence of bioactive elements Ca and P were detected. The thickness of the coatings obtained by PEO increases drastically for voltages higher than 250 V (from 4.50 ± 0.33 to 23.83 ± 1.5 µm). However, coatings obtained with lower voltages presented thin and dense layers, which promoted a superior wear resistance (increase in wear rate from 1.99 × 10⁻⁶ to 2.60 × 10⁻⁵ mm³/s). Finally, compared to the uncoated substrate, the PEO coatings increased the wear resistance of the titanium alloy obtained by AM, also showing a superior wear resistance compared to the commercial Ti-6Al-4V alloy previously evaluated, being such a positive and promising behavior for application in the area of metallic implants.

We investigate the magnetization dynamics through the magnetoimpedance effect in ferromagnetic NiFe/Cu/Co films. We observe that the magnetoimpedance response is dependent on the thickness of the non-magnetic Cu spacer material. We verify asymmetric magnetoimpedance in films with biphase magnetic behavior and explore the possibility of tuning the linear region of the magnetoimpedance curves around zero magnetic field by varying the thickness of the spacer and probe current frequency. We discuss the experimental results in terms of the different mechanisms governing the magnetization dynamics at distinct frequency ranges, quasi-static magnetic properties, thickness of the spacer, and the kind of the magnetic interaction between the ferromagnetic layers. The results place films with biphase magnetic behavior exhibiting asymmetric magnetoimpedance effect as very attractive candidates for application as probe element in the development of auto-biased linear magnetic field sensors.

The submicrosecond dynamics of thermomagnetic avalanches in superconducting films with nonconducting holes (antidots) is considered. When such an avalanche reaches a hole, it is quickly filled with magnetic flux, and often its rim becomes unstable and a second avalanche is nucleated. In this work the time- and space-resolved behavior of such cascading avalanche behavior is determined using numerical simulations. Results are presented for films with holes of different shape. It is found that holes with sharp corners are those that most frequently create secondary avalanches, and they tend to nucleate in corners. Magneto-optical imaging of Nb films patterned with the same set of holes strongly supports the numerical results.