In this study, multi-walled carbon nanotubes (MWCNTs) were chemically modified using three acid treatment methods to introduce the surface oxygen functional group (SOFG). The presence of SOFG on the MWCNTs has been characterized by Fourier Transform Infrared (FTIR) spectroscopy. Morphology, structural and thermal properties were performed using Field Emission Scanning Electron Microscopy (FESEM), Raman spectroscopy, and Thermogravimetric analysis (TGA), respectively. The result shows that the modification with acid treatment significantly affects the degree of defects and surface group functionality of surface oxidized MWCNTs from method B. The preparation of nanofluids using MWCNTs produced from method B (MWCNT-MB) was prepared using two different parameters: with and without polyvinylpyrrolidone (PVP) as surfactant. The experiment was conducted by setting variable carbon particle concentration from 0.1 wt.% to 1.0 wt.%, and the amount of PVP is 10% of carbon particles at different temperatures (6 °C, 25 °C, 40 °C). Based on visual observation, the dispersion of carbon particles was enhanced by the presence of PVP as the stabilizing agent. The thermal conductivity performance of nanofluids revealed that the surface oxidized MWCNTs with PVP show enhanced thermal conductivity compared to the nanofluid containing MWCNTs without PVP. The improvement contributes to this in terms of stability and homogenization of nanoparticles. Hence the improved distribution of MWCNTs in water-based media improves thermal conductivity. These promising properties of MWCNTs in water-based fluids would enable the nanofluids to be used in heat transfer fluid and cooling applications.

Chemical sensors are a rapidly developing technology that has received much attention in diverse industries such as military, medicine, environmental surveillance, automotive power and mobility, food manufacturing, infrastructure construction, product packaging and many more. The mass production of low-cost devices and components for use as chemical sensors is a major driving force for improvements in each of these industries. Recently, studies have found that using renewable and eco-friendly materials would be advantageous for both manufacturers and consumers. Thus, nanotechnology has led to the investigation of nanocellulose, an emerging and desirable bio-material for use as a chemical sensor. The inherent properties of nanocellulose, its high tensile strength, large specific surface area and good porous structure have many advantages in its use as a composite material for chemical sensors, intended to decrease response time by minimizing barriers to mass transport between an analyte and the immobilized indicator in the sensor. Besides which, the piezoelectric effect from aligned fibers in nanocellulose composites is beneficial for application in chemical sensors. Therefore, this review presents a discussion on recent progress and achievements made in the area of nanocellulose composites for chemical sensing applications. Important aspects regarding the preparation of nanocellulose composites using different functionalization with other compounds are also critically discussed in this review.

Chlorine gas is extensively utilised in industries as both a disinfectant and for wastewater treatment. It has a pungent and irritating odour that is comparable with that of bleach and can cause serious health issues such as headaches and breathing difficulties. Hence, efficiently, and accurately monitoring chlorine gas is critical to ensure that no undesirable incidents occur. Due to its remarkable characteristics, numerous researchers have explored the potential of ferrite nanoparticles as a sensing material for chlorine gas detection. Among several ferrite nanoparticles, nickel ferrite (NiFe₂O₄) is extensively studied as an inverse spinel structured magnetic material that may be ideal for sensing applications. However, the magnetic characteristics of NiFe₂O₄ cause agglomeration, which necessitates the use of a substrate for stabilisation. Therefore, nanocellulose (NC), as a green and eco-friendly substrate, is ideal for stabilising bare nickel ferrite nanoparticles. In a novel experiment, nickel ferrite was loaded onto NC as a substrate using in situ deposition. The structure was confirmed by X-ray Diffraction (XRD) analysis, while elemental composition was verified by Energy dispersive X-ray (EDX) analysis. Gas sensing properties were determined by evaluating sensitivity as a function of various regulating factors, such as the amount of nickel ferrite, gas concentration, repeatability, and reusability. In the evaluation, 0.3 g nickel ferrite showed superior response and sensitivity than those of other samples. The achieved response time was around 40 s, while recovery time was about 50 s. This study demonstrates the potential of a nickel ferrite/nanocellulose-based nanocomposite to efficiently monitor chlorine gas.

In this paper, carbon nanotubes (CNTs) were functionalized by acid treatment and further functionalized with dodecylamine and were designated as CNT-carboxylic and CNT-amide, respectively. Then, functionalized CNTs produced were characterized with various methods to verify the attachment of a functional group. Performance of the functionalized CNTs in the detection of benzene gas was monitored at room temperature. The sample was dropped cast on the interdigitated transducer (IDT), and the changes in resistivity were recorded by a digital multimeter in a customized chamber under controlled humidity (∼55%) environment. Based on the findings, it showed that the functionalized CNTs provide an extra active area for interaction between the gas analyte and CNTs, thus increasing their response and improving the sensitivity of the sensing material.

Chlorine gas is a greenish-yellow gas that is one of the most utilized gases in numerous industrial fields. It has been categorized as a choking agent that can threaten human, animal, and environmental safety. Currently, development of highly sensitive, selective, and precise chlorine sensors receives much attention. This review focuses on several sensing techniques used for chlorine gas and free chlorine in water. The fundamental working principles, as well as the sensing mechanisms of chlorine detection covering spectrophotometric, electrochemical, and optical techniques, are described. A comparison of various sensing materials is also discussed. Finally, an overview of the future improvements needed of high-performance chlorine sensors was suggested.

The reputation of nanofluids as a convenient heat transfer media has grown in recent years. The synthesis of nanofluids is often challenging, particularly carbon-based nanofluids, due to the rapid agglomeration of the nanoparticles and the instability of the nanofluids. In this regard, surface modification and surfactant addition are potential approaches to improve the physical and thermal properties of carbon-based nanofluids that have been studied and the structural, morphological, and thermal characteristics of surface-oxidised carbon nanofibre (CNF)-based nanofluids has been characterised. Commercial CNF was first subjected to three different acid treatments to introduce surface oxygen functional groups on the CNF surface. Following the physical and thermal characterisation of the three surface-oxidised CNFs (CNF-MA, CNF-MB, and CNF-MC), including Raman spectroscopy, Fourier transform infrared (FTIR), thermogravimetric analysis (TGA), and field emission scanning electron microscopy (FESEM), the CNF-MB was selected as the best method to synthesise the surface-oxidised CNF-based nanofluid. A total of 40 mL of ultrapure water was used as a pure base fluid and mixed with the surface-oxidised CNF at a concentration range of 0.1–1.0 wt.%, with a fixed of 10 wt.% amount of polyvinylpyrrolidone (PVP). The thermal conductivity of CNF-based nanofluid was then characterised at different temperatures (6, 25, and 40 °C). Based on the results, surface oxidation via Method B significantly affected the extent of surface defects and effectively enhanced the group functionality on the CNF surface. Aside from the partially defective and rough surface of CNF-MB surfaces from the FESEM analysis, the presence of surface oxygen functional groups on the CNF wall was confirmed via the Raman analysis, TGA curve, and FTIR analysis. The visual sedimentation observation also showed that the surface-oxidised CNF particles remained dispersed in the nanofluid due to the weakened van der Waals interaction. The dispersion of CNF particles was improved by the presence of PVP, which further stabilised the CNF-based nanofluids. Ultimately, the thermal conductivity of the surface-oxidised CNF-based nanofluid with PVP was significantly improved with the highest enhancement percentage of 18.50, 16.84, and 19.83% at 6, 25, and 40 °C, respectively, at an optimum CNF concentration of 0.7 wt.%.