High-entropy herringbone alloy: Eutectic high-entropy alloys have a dual phase structure that could be useful for optimizing a material’s properties. Shi et al . found that directional solidification of an aluminum-iron-cobalt-nickel eutectic high-entropy alloy created a herringbone-patterned microstructure that was extremely resistant to fracture (see the Perspective by An). The structure contained lamellae of hard and soft phases, and the cracks that formed in the hard phase were arrested at the boundary of the soft phase. This, along with stress transfer, allowed a tripling of the maximal elongation while retaining high strength. —BG

Laser shock peening (LSP) is an innovative surface treatment process with the potential to change surface microstructure and improve mechanical properties of additively manufactured (AM) parts. In this paper, the influences of LSP on the microstructure and properties of Ti–6Al–4V (Ti64) titanium alloy fabricated via selective laser melting (SLM), as an attractive AM method, were investigated. The microstructural evolution, residual stress distribution and mechanical properties of SLM-built Ti64 samples were characterized before and after LSP. Results show that the SLM sample was composed of single hcp α’ phase, which deviates from equilibrium microstructure at room temperature: α + β phases. The LSP significantly refines the grains of α’ phase and produces compressive residual stress (CRS) of maximum magnitude up to −180 MPa with a depth of 250 μm. Grain refinement of α’ phase is attributed to the complex interaction of dislocations and the intersection of deformation twinning subjected to LSP treatment. The main mechanism of strength and micro-hardness enhancement via LSP is ascribed to the effects of CRS and α’ phase grain refinement.

Eutectic high-entropy alloys (EHEAs) feature attractive strength–ductility balance at both ambient and cryogenic temperatures. Nevertheless, microstructural origins underpinning these balanced mechanical properties remain elusive. Here the deformation mechanisms of a recently-reported Al₁₉Co₂₀Fe₂₀Ni₄₁ EHEA were comparatively investigated at 298 and 77 K, which revealed a high frequency and density of dislocation multi-slip scenario in the soft eutectic lamellae and the corresponding compatible co-deformation in the adjacent hard lamellae that collectively endowed strong hetero-deformation-induced (HDI) hardening and excellent forest-dislocation hardening. Therefore, better ductility and tensile strength, in comparison to the other widely-studied EHEA system, could be sustained even at liquid-nitrogen temperatures. GRAPHICAL ABSTRACT IMPACT STATEMENT We identify a new eutectic HEA system with superior strength–ductility combination at liquid-nitrogen temperatures, and provide critical microstructural insights and mechanisms into its enhanced cryogenic properties.

The present study investigates the morphological evolution of carbonitrides and the effect of these precipitates on grain boundary pinning during pseudo-carburizing a Nb-Ti-Al microalloyed steel. The result indicated that three kinds of complex precipitates with different morphologies containing Nb, Ti, and Al respectively were observed in samples austenitized at different temperatures and times. The NbC and TiN precipitates played an important role in pinning grain boundaries and suppressing the growth of austenite grains, relying on the high thermal stability of TiN precipitates and small size of NbC precipitates. The precipitate characteristics affected the size of austenite grain. Based on the Zener pinning model, the effect of precipitate characteristic on austenite grain size was quantitatively analyzed. It is found that the existence of NbC and TiN precipitated at high temperature makes austenite grain growth difficult when austenite grain boundaries were pinned by fine and diffused precipitates.

Accompanied by the formation of pearlite, Widmanstätten ferrite (WF), grain boundary ferrite and cementite are often found to nucleate at the prior austenite grain boundary during isothermal heat treatment. A hypereutectoid pearlitic steel transformed isothermally at temperatures ranging from 607 to 707 °C was investigated to clarify the evolution of different phases. At 607 °C, WF grains, which had a Kurdjumov–Sachs orientation relationship with the remaining austenite, were found to be aligned with the grain boundary. At 707 °C, lath WF grains, which were arranged parallel to each other, were at a certain angle to the grain boundary. The formation of pearlite showed two-stage kinetics in the dilatometer curve, and the grain boundary’s abnormal structure was suppressed.