Oh, now I see! The precipitates formed during Th^IV hydrolysis are ThO₂ nanoparticles, which in their initial stages of formation are a mixture of ultra‐small nanoparticles and Th hexamer clusters. This new structural insight is made possible by the combined use of two synchrotron techniques: HEXS and XANES in HERFD mode, which probe short‐ and medium‐range order in the sample under study. More information can be found in the Full Paper by L. Amidani et al. (DOI: 10.1002/chem.202003360).

The structural characterisation of actinide nanoparticles (NPs) is of primary importance and hard to achieve, especially for non‐homogeneous samples with NPs less than 3 nm. By combining high‐energy X‐ray scattering (HEXS) and high‐energy‐resolution fluorescence‐detected X‐ray absorption near‐edge structure (HERFD XANES) analysis, we have characterised for the first time both the short‐ and medium‐range order of ThO₂ NPs obtained by chemical precipitation. By using this methodology, a novel insight into the structures of NPs at different stages of their formation has been achieved. The pair distribution function revealed a high concentration of ThO₂ small units similar to thorium hexamer clusters mixed with 1 nm ThO₂ NPs in the initial steps of formation. Drying the precipitates at around 150 °C promoted the recrystallisation of the smallest units into more thermodynamically stable ThO₂ NPs. HERFD XANES analysis at the thorium M₄ edge, a direct probe for f states, showed variations that we have correlated with the breakdown of the local symmetry around the thorium atoms, which most likely concerns surface atoms. Together, HEXS and HERFD XANES are a powerful methodology for investigating actinide NPs and their formation mechanism.

The compound BiFe_0.7Mn_0.3O₃ consisting at room temperature of coexistent anti-polar orthorhombic and polar rhombohedral phases has a metastable structural state, which has been studied by laboratory X-ray, synchrotron and neutron diffraction, magnetometry, differential thermal analysis, and differential scanning calorimetry. Thermal annealing of the sample at temperatures above the temperature-driven phase transition into the single phase rhombohedral structure (~700 K) causes an increase of the volume fraction of the rhombohedral phase at room temperature from ~10% up to ~30%, which is accompanied by the modification of the magnetic state, leading to strengthening of a ferromagnetic component. A strong external magnetic field (~5 T) applied to the sample notably changes its magnetic properties, as well as provides a reinforcement of the ferromagnetic component, thus leading to an interaction between two magnetic subsystems formed by the antiferromagnetic matrix with non-collinear alignment of magnetic moments and the nanoscale ferromagnetic clusters coexisting within it. The modification of the structural state and magnetic properties of the compounds and a correlation between different structural and magnetic phases are discussed focusing on the effect of thermal annealing and the impact of an external magnetic field.