A new series of thin film composite membranes with high CO₂ permeance (up to 8000 GPU) and CO₂/N₂ selectivity (up to 55.7) was designed and fabricated via coating PIM-1 solution in a mixture of chloroform and trichloroethylene on top of a cross-linked PTMSP gutter layer.

Palm or coconut oil is capable of dissolving in a mixture of bisphenol A-based epoxy resin and a high-temperature hardener (4,4′-diaminodiphenyl sulfone) when heated and then forms a dispersed phase as a result of cross-linking and molecular weight growth of the epoxy medium. Achieving the temporary miscibility between the curing epoxy matrix and the vegetable oil allows a uniform distribution of vegetable oil droplets in the epoxy medium. This novel approach to creating a dispersed phase-change material made a cured epoxy polymer containing up to 20% oil. The miscibility of epoxy resin and oil was studied by laser interferometry, and phase state diagrams of binary mixtures were calculated according to theory and experiments. A weak effect of oil on the viscosity and kinetics of the epoxy resin curing was demonstrated by rotational rheometry. According to differential scanning calorimetry and dynamic mechanical analysis, the oil plasticizes the epoxy matrix slightly, expanding its glass transition region towards low temperatures and reducing its elastic modulus. In the cured epoxy matrix, oil droplets have a diameter of 3–14 µm and are incapable of complete crystallization due to their multi-component chemical composition and non-disappeared limited miscibility. The obtained phase-change materials have relatively low specific energy capacity but can be used alternatively as self-lubricating low-noise materials due to dispersed oil, high stiffness, and reduced friction coefficient. Palm oil crystallizes more readily, better matching the creation of phase-change materials, whereas coconut oil crystallization is more suppressed, making it better for reducing the friction coefficient of the oil-containing material.

The low thermal conductivity of paraffin and other organic phase change materials limits their use in thermal energy storage devices. The introduction of components with a high thermal conductivity such as graphene into these materials leads to an increase in their thermal conductivity. In this work, we studied the use of inexpensive carbon fillers containing a polycyclic aromatic core, due to them having a structural similarity with graphene, to increase the thermal conductivity of paraffin. As such fillers, technogenic asphaltenes isolated from ethylene tar and their modified derivatives were used. It is shown that the optimal concentration of carbon fillers in the paraffin composite, which contributes to the formation of a structural framework and resistance to sedimentation, is 5 and 30 wt. %, while intermediate concentrations are ineffective, apparently due to the formation of large aggregates, the concentration of which is insufficient to form a strong framework. It has been found that the addition of asphaltenes modified with ammonium persulfate in acetic acid significantly increases the thermal conductivity of paraffin by up to 72%.

Adding carbon nanoparticles into organic phase change materials (PCMs) such as paraffin is a common way to enhance their thermal conductivity and to improve the efficiency of heat storage devices. However, the sedimentation stability of such blends can be low due to aggregation of aromatic carbon nanoparticles in the aliphatic paraffin environment. In this paper, we explore whether this important issue can be resolved by the introduction of a polymer agent such as poly(3-hexylthiophene) (P3HT) into the paraffin–nanoparticle blends: P3HT could ensure the compatibility of aromatic carbon nanoparticles with aliphatic paraffin chains. We employed a combination of experimental and computational approaches to determine the impact of P3HT addition on the properties of organic PCMs composed of paraffin and carbon nanoparticles (asphaltenes). Our findings clearly show an increase in the sedimentation stability of paraffin–asphaltene blends, when P3HT is added, through a decrease in average size of asphaltene aggregates as well as in an increase of the blends’ viscosity. We also witness the appearance of the yield strength and gel-like behavior of the mixtures. At the same time, the presence of P3HT in the blends has almost no effect on their thermophysical properties. This implies that all properties of the blends, which are critical for heat storage applications, are well preserved. Thus, we demonstrated that adding polyalkylthiophenes to paraffin–asphaltene mixtures led to significant improvement in the performance characteristics of these systems. Therefore, the polymer additives can serve as promising compatibilizers for organic PCMs composed of paraffins and asphaltenes and other types of carbon nanoparticles.