This study evaluated the impact of using biomimetic analogs (poly-acrylic acid and sodium tri-meta-phosphate) on dentin remineralization using two cement materials, the first is calcium silicate based and the second is calcium hydroxide based materials. Two standardized occlusal cavities (mesial and distal) were prepared within dentin after removal of occlusal enamel. Artificial demineralized dentin was induced through pH cycling (8 h in demineralizing and 16 h in remineralizing solutions). Demineralized cavities were divided into four groups; two groups received cement materials. The other groups were first treated with biomimetic analogs then restored with pulp cement materials. Teeth were sectioned buccolingually into two halves. Treated cavities with analogs were stored in simulated body fluid containing poly-acrylic acid. Untreated cavities were stored in simulated body fluid only. Ground unstained sections of demineralized dentin were examined using light microscope. Specimens were examined after 1, 6 and 12 weeks of storage using energy dispersive X-ray Spectroscopy (EDX) and Vickers microhardness was evaluated. Two-way ANOVA was used to analyze data statistically. Calcium silicate-based cement group with biomimetic analogs showed the highest statistically significant calcium and phosphorous wt% in addition to highest surface hardness values after 12 weeks of storage. Demineralized dentin ground sections showed increase in light zones after total period of storage. Calcium silicate-based cement showed the best ability to enrich the artificial carious dentin with ions for remineralization. Using biomimetic analogs had a significant impact on demineralized dentin surface hardness improvement.

Background: Flexible denture base polymers have gained popularity in modern dentistry however, their biofilm formation tendency, adversely affecting the oral tissue heath, remains a concern. Consequently, this study aimed to evaluate surface roughness and biofilm formation tendency of two types of denture base resins manufactured with two techniques before and after surface coating with chlorohexidine (CHX) NPs. Materials and methods: Acetal (AC) and Polymethyl-methacrylate (PMMA) resins manufactured by conventional and CAD/CAM methods were shaped into disk (10 X 10 X 1 mm). They were dipped for 8 h and 24 h in colloidal suspension prepared by mixing aqueous solution of CHX digluconate and hexa-metaphosphate (0.01 M). Surface roughness, optical density (OD) of microbial growth media and biofilm formation tendency were evaluated directly after coating. Elutes concentrations of released CHX were evaluated for 19 days using spectrophotometer. Three-way ANOVA and Tukey’s post-hoc statistical analysis were used to assess the outcomes. Results: AC CAD/CAM groups showed statistically significant higher roughness before and after coating (54.703 ± 4.32 and 77.58 ± 6.07 nm, respectively). All groups showed significant reduction in OD and biofilm formation tendency after surface coating even after 19 days of CHX NPs release. Conclusions: Biofilm formation tendency was highly relevant to surface roughness of tested resins before coating. After CHX NPs coating all tested groups showed significant impact on microbial growth and reduction in biofilm formation tendency with no relation to surface roughness. Significant antimicrobial effect remained even after 19 days of NPs release and specimens storage.

Background/Objectives: Fabrication of ceramic restorations with higher performance, biocompatibility, and mechanical durability, as well as excellent optical properties, is challenging. Therefore, this study was designed to investigate the mechanical properties and surface roughness of different glass ceramics manufactured with CAD/CAM and pressed techniques before and after exposure to simulated gastric acidic challenge. Methods: Lithium disilicate-based (LDS) ceramic, advanced lithium disilicate (ALDS), and zirconia-reinforced lithium silicate (ZLSC), were manufactured with two techniques. Disc-shaped (N = 336) specimens were used to test the biaxial flexural strength (BFS), while surface microhardness and surface roughness were evaluated before and after exposure to hydrochloric acid (34–37% concentration and 1.2 pH for 24 h). The results were statistically evaluated using two- and one-way ANOVA, Tukey’s post-hoc and Student’s t-test. Results: Both CAD and pressed types of LDS ceramic IPS e.max, showed significantly highest BFS and microhardness before and after acidic challenge (p = 0.01 and <0.01, respectively). ALDS and ZLSC showed significantly lower roughness before acidic aging, while all groups showed no significant difference after aging. Conclusion: Pressed groups showed better mechanical performance than CAD groups. LSD (IPS e.max types) continuously showed a better mechanical performance than modified LDS. ALDS and ZLSC showed the best performance in terms of surface smoothness, but after acidic exposure, no significant difference was observed compared to the other groups.