Hemp fibres used as a reinforcing agent and three polymeric matrices (polypropylene, bicomponent, recycled polyester) were used to obtain composite materials by needle punching and heat pressing. The influence of the hemp/matrix ratio and the nature of the matrix on the properties of the composites were analysed. The obtained composites were characterised by physical–mechanical indices, thermal analysis (thermogravimetry (TG), differential thermogravimetry (DTG) and Differential Scanning Calorimetry (DSC)), Fourier Transform Infrared Spectroscopy (FTIR-ATR) analysis, Scanning Electron Microscopy (SEM) and Chromatic measurements. The mechanical properties of composites are influenced by both the hemp/matrix ratio and the nature of the matrix. The thermal stability of composites decreased as the amount of hemp increased (for the same mass losses, the decomposition temperature decreased significantly for composites containing a quantity of hemp greater than 50%). Regarding the nature of the matrix, for the same mass loss, the highest decomposition temperature was presented by the composites containing recycled polyester as matrix, and the lowest one was presented by composites containing polypropylene fibres as matrix. The FTIR and SEM analyses highlight the changes that occurred in the structure of the composite, changes determined both by the amount of hemp in the composite and by the nature of the matrix.

The objective of the work was to obtain materials with aromatherapeutic and antibacterial properties by applying emulsions based on peppermint essential oil (PEO) onto cotton fabric. For this purpose, some emulsions based on PEO incorporated in various matrices (chitosan + gelatin + beeswax; chitosan + beeswax; gelatin + beeswax and gelatin + chitosan) were prepared. Tween 80 was used as a synthetic emulsifier. The influence of the nature of matrices and of the concentration of Tween 80 on the stability of the emulsions was evaluated by the creaming indices. The materials treated with the stable emulsions were analyzed in terms of sensory activity, of the comfort characteristics, and of the gradual release of the PEO in the artificial perspiration solution. The sum of volatile components retained by samples after exposure to air was determined by GC-MS. The results regarding antibacterial activity showed that materials treated with emulsions have a good inhibitory effect on S. aureus (diameters of the inhibition zones between 53.6 and 64.0 mm) and on E. coli (diameters of the inhibition zones between 38.3 and 64.0 mm). Our data suggest that by applying peppermint-oil-based emulsions on a cotton support, aromatherapeutic patches, bandages and dressings with antibacterial properties can be obtained.