This work aimed to review the recent scientific research, focused on the application of recycled fibers, taken from textile waste, in the field of composite materials to fulfill the eco-sustainability requirements of textile manufacturing, and promote actions for a circular economy. The yarns and fabric production represent one of the most polluting processes of the industrial world. The harmful environmental impact of the textile process has been described by reporting the different treatments involving the raw material and the filament fabrication, and concerning the uses of insecticides, fertilizers, and many other chemicals for improving the quality of the final products. In addition, solid textile waste constituted a further additional issue for the environmental sustainability of fabric production. Various strategies have been discussed and in part already adopted by many companies to recover waste fibers and prevent them from ending up in landfills. The alternatives of fiber recycling for composite realization have been presented by reporting several recent studies involving the uses of recycled fibers from the textile waste embedded in different matrices: thermoplastic polymer, thermosetting resins, natural constituents, and concrete in light of specific applications.

Three commercial filaments for Fused Deposition Modeling (FDM) were selected to study the influence of polymer formulation on the printing quality and mechanical properties of FDM specimens. The three filaments were all based on polylactic acid (PLA) as the matrix, and they are sold as PLA filaments. The printing quality was tested by printing one complex shape with overhang features. The marked shear thinning behavior for two filaments was observed by rheology. The filaments were also studied by scanning electron microscopy and thermogravimetric analysis (TGA) to unveil their composition. The filaments with the best printing quality showed the presence of mineral fillers, which explained the melt behavior observed by rheology. The tensile testing confirmed that the filled PLA was the best-performing filament both in terms of printing quality and thermomechanical performance, with a p-value = 0.106 for the tensile modulus, and a p-value = 0.615 for the ultimate tensile strength.