Three commercial filaments for Fused Deposition Modeling (FDM) were selected to study the influence of polymer formulation on the printing quality and mechanical properties of FDM specimens. The three filaments were all based on polylactic acid (PLA) as the matrix, and they are sold as PLA filaments. The printing quality was tested by printing one complex shape with overhang features. The marked shear thinning behavior for two filaments was observed by rheology. The filaments were also studied by scanning electron microscopy and thermogravimetric analysis (TGA) to unveil their composition. The filaments with the best printing quality showed the presence of mineral fillers, which explained the melt behavior observed by rheology. The tensile testing confirmed that the filled PLA was the best-performing filament both in terms of printing quality and thermomechanical performance, with a p-value = 0.106 for the tensile modulus, and a p-value = 0.615 for the ultimate tensile strength.

The exploitation of mechanical properties and customization possibilities of 3D printed metal parts usually come at the cost of complex and expensive equipment. To address this issue, hybrid metal/polymer composite filaments have been studied allowing the printing of metal parts by using the standard Fused Filament Fabrication (FFF) approach. The resulting hybrid metal/polymer part, the so called “green”, can then be transformed into a dense metal part using debinding and sintering cycles. In this work, we investigated the manufacturing and characterization of green and sintered parts obtained by FFF of two commercial hybrid metal/polymer filaments, i.e., the Ultrafuse 316L by BASF and the 17-4 PH by Markforged. The Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectrometry (EDS) analyses of the mesostructure highlighted incomplete raster bonding and voids like those observed in conventional FFF-printed polymeric structures despite the sintering cycle. A significant role in the tensile properties was played by the building orientation, with samples printed flatwise featuring the highest mechanical properties, though lower than those achievable with standard metal additive manufacturing techniques.

This research focuses on the thermal characterization of 3D-printed parts obtained via fused filament fabrication (FFF) technology, which uses a poly(lactic acid) (PLA)-based filament filled with milled carbon fibers (MCF) from pyrolysis at different percentages by weight (10, 20, 30 wt%). Differential scanning calorimetry (DSC) and thermal conductivity measurements were used to evaluate the thermal characteristics, morphological features, and heat transport behavior of the printed specimens. The experimental results showed that the addition of MCF to the PLA matrix improved the conductive properties. Scanning electron microscopy (SEM) micrographs were used to obtain further information about the porosity of the systems.

Metal 3D-printed parts are critical in industries such as biomedical, surgery, and prosthetics to create tailored components for patients, but the costs associated with traditional metal additive manufacturing (AM) techniques are typically prohibitive. To overcome this disadvantage, more cost-effective manufacturing processes are needed, and a good approach is to combine fused deposition modeling (FDM) with debinding-sintering processes. Furthermore, optimizing the printing parameters is required to improve material density and mechanical performance. The design of experiment (DoE) technique was used to evaluate the impact of three printing factors, namely nozzle temperature, layer thickness, and flow rate, on the tensile and bending properties of sintered 316L stainless steel in this study. Green and sintered samples were morphologically and physically characterized after printing, and the optimal printing settings were determined by statistical analysis, which included the surface response technique. The mechanical properties of the specimens increased as the flow rate and layer thickness increased and the nozzle temperature decreased. The optimized printing parameters for the ranges used in this study include 110% flow rate, 140 μm layer thickness, and 240 °C nozzle temperature, which resulted in sintered parts with a tensile strength of 513 MPa and an elongation at break of about 60%.

Green composites from polypropylene and lignin-based natural material were manufactured using a melt extrusion process. The lignin-based material used was the so called “liquid wood”. The PP/“Liquid Wood” blends were extruded with “liquid wood” content varying from 20 wt % to 80 wt %. The blends were thoroughly characterized by flexural, impact, and dynamic mechanical testing. The addition of the Liquid Wood resulted in a great improvement in terms of both the flexural modulus and strength but, on the other hand, a reduction of the impact strength was observed. For one blend composition, the composites reinforced with hemp fibers were also studied. The addition of hemp allowed us to further improve the mechanical properties. The composite with 20 wt % of hemp, subjected to up to three recycling cycles, showed good mechanical property retention and thermal stability after recycling.