To solve the issues of insufficient early strength of cement stabilized soil and high resource cost, high reduction cost, and high environmental cost induced by the application of cement, the slag and fly ash-based geopolymer was adopted as the stabilizer to treat riverside soft soil. This study mainly investigated the effects of stabilizer content, slag-to-fly ash ratio, and alkaline activator content on the strength of geopolymer stabilized soils with different curing ages. Unconfined compressive strength (UCS), scanning electron microscope (SEM), and X-ray energy spectrum analysis (EDS) tests were carried out. The results show that the stabilizer content, slag–fly ash ratio, and alkaline activator content have a decisive influence on the UCS of geopolymer-stabilized soil. The mix-proportions scheme of geopolymer stabilized riverside soft soil, with a geopolymer content of 15%, a slag–fly ash ratio of 80:20, and an alkaline activator content of 30%, is considered optimum. It is proven by SEM that the uniformly distributed gelatinous products formed in the geopolymer-stabilized soil bind the soil particles tightly. Moreover, the EDS analysis confirms that the gelatinous products are mainly composed of C-S-H gel and sodium-based aluminosilicate (N-A-S-H).

The preparation of ultra-high-performance concrete (UHPC) with both high-early-strength and good workability contributes to further promotion of its development and application. This study investigated the effects of different accelerators (SM, alkaline powder accelerator; SF, alkaline powder accelerator containing fluorine; and AF, alkali-free liquid accelerator containing fluorine) on the workability and strength properties of UHPC. The microstructure of UHPC was also characterized by using XRD and SEM. Several dosage levels of accelerators (2%, 4%, 6%, and 8% by mass) were selected. The results indicate that the setting time and fluidity of UHPC are gradually decreased with an increase in accelerators dosage. Compared with fluorine-containing SF/AF, fluorine-free SM evidently facilitates UHPC early strength gain speed. However, the fluorine-containing accelerators have a higher 28 d strength ratio, especially AF. The maximum compressive and flexural strength ratios are obtained at a dosage of 6%, which are 95.5% and 98.3%, respectively. XRD and SEM tests further reveal the effect of different accelerators on the macroscopic properties of UHPC from the micro level.

Geopolymer, as a new type of solid waste-based inorganic cementitious material, exhibits outstanding behavior in terms of physical and chemical performance, macromechanical properties, long-lasting stability, and features potential application development tendency in the field of repair and reinforcement of existing concrete structures. This paper investigated the interfacial behavior of geopolymer mortar with OPC concrete substrate under different slag, fly ash and red mud mixing proportions, while cement mortar was used as a control group for the research. The interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate were elaborated by carrying out split tensile test, double-sided shear test, and three-point bending test. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were employed to further analyze the microstructural characteristics and physical phase components of the interfacial transition zone between the geopolymer mortar and the OPC concrete substrate. The results indicated that the compressive strength of slag-fly ash-red mud-based geopolymer mortar under different mixing ratio conditions was consistently superior to that of cement mortar, where the optimum mixing ratio for the geopolymer mortar was S33F33R33. Overall, the interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate gradually increased with the increment of the slag content, however, an evolutionary trend of minor enhancement followed by a gradual reduction was observed with the growth of the fly ash and red mud content.

Sulfate attack is one of the non-negligible factors that induces deterioration in the performance and life cycle of soil stabilizers. In this paper, the degradation mechanism of the durability of slag–fly-ash-based geopolymer stabilized soft soil (hitherto referred to as SF-GSSS) under the sodium sulfate (Na₂SO₄) and magnesium sulfate (MgSO₄) attack environment is comparatively investigated, and the slag/fly ash ratios are set to S10F0, S9F1, S8F2, and S7F3. The SF-GSSS was fully immersed in a 2.5% Na₂SO₄ solution and 2.5% MgSO₄ solution, respectively, to characterize the deterioration rules via visual observations, an unconfined compressive strength (UCS) test, and by mass change. The effect of sulfate on the microstructural characteristics of the SF-GSSS were determined by different microanalytical means, such as by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the SF-GSSS immersed in a MgSO₄ solution displayed significant physical deterioration, but not when in a Na₂SO₄ solution. The mass growth of the SF-GSSS when immersed in a Na₂SO₄ solution was significantly lower than when it was immersed in a MgSO₄ solution at the same immersion age. The rate of strength loss was lowest for S9F1 and highest for S7F3 at the end of immersion, regardless of its immersion in Na₂SO₄ or MgSO₄ solutions.

The complexity of composite geopolymer materials results in instability in the setting and hardening of geopolymer-stabilized soil. In order to determine the appropriate mix proportion scheme for composite geopolymer-stabilized soil, this study investigated the effects of two preparation methods, fly ash/slag ratio and alkali activator modulus, on workability and strength development trends in alkali-excited fly ash and slag-based geopolymer-stabilized soil. The results showed that the high ambient temperatures created by the one-step method were more conducive to the setting and hardening of the geopolymer-stabilized soil; its 3 d/28 d UCS (unconfined compression strength) ratio was 62.43–78.60%, and its 7 d/28 d UCS ratio was 70.37–83.63%. With increases of the alkali activator modulus or the proportion of fly ash, the setting time of stabilized soil was gradually prolonged, and its fluidity increased. Meanwhile, the strength development of stabilized soil was significantly affected by the proportion of fly ash and the alkali activator modulus; the maximum UCS value was obtained at II-2-O, prepared by the one-step method, with an alkali activator modulus of 1.2 and a fly ash/slag ratio of 20/80. Specifically, the 3, 7, and 28 d UCS values of II-2-O were 1.65, 1.89, and 2.26 MPa, respectively, and its 3 d/28 d UCS ratio and 7 d/28 d UCS ratio were 73.01% and 83.63%, respectively. These results will be of great importance in further research on (and construction guidance of) composite geopolymer-stabilized soil.

Geopolymer, as a new type of solid waste-based inorganic cementitious material, exhibits outstanding Behavior in terms of physical and chemical performance, macro-mechanical properties and long-lasting stability, and features potential application development tendency in the field of repair and reinforcement of existing concrete structures. This paper investigates the interfacial Behavior of geopolymer mortar with OPC concrete substrate under different slag, fly ash and red mud mixing proportions, while cement mortar was used as a control group for the research. The interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate were elaborated by carrying out split tensile test, two-sided shear test and three-point bending test. The scanning electron microscopy (SEM) and X-ray diffraction (XRD) were employed to further analyse the microstructural characteristics and physical phase components of the interfacial transition zone between the geopolymer mortar and the OPC concrete substrate. The results indicated that the compressive strength of slag-fly ash-red mud-based geopolymer mortar under different mixing ratio conditions was consistently superior to that of cement mortar. Overall, the interfacial bonding properties of the geopolymer mortar to the OPC concrete substrate gradually increased with the increment of the slag content, however, an evolutionary trend of minor enhancement followed by a gradual reduction was observed with the growth of the fly ash and red mud content.