Our review covers the achievements of recent decades in the investigation of the acid-base properties of oxide catalyst surfaces. Both conventional and new investigation techniques are reviewed,...

Two series of Ni/Ce(Ti/Nb)ZrO₂ catalysts were prepared using citrate route and original solvothermal continuous flow synthesis in supercritical isopropanol and studied in dry reforming of methane (DRM). TEM, XPS and FTIRS of adsorbed CO confirm influence of support composition and preparation method on the catalysts’ morphology and surface features. The oxygen mobility was studied by isotope heteroexchange with C¹⁸O₂. After testing in DRM, carbon deposits after catalysts’ testing in DRM were investigated by temperature-programmed oxidation with thermo-gravimetric analysis. The lowest amounts of carbon deposits were obtained for unmodified Ni-CeZr and Ni-CeNbZr compositions. Ti addition lead to an increased amount of carbon, which was removed at higher temperatures. The use of supercritical supports also resulted in the formation of a higher amount of coke. Catalysts prepared by the supercritical synthesis were tested in DRM for 25 h. The highest activity drop was observed in the first three hours. For all compositions, close values of carbon deposits were revealed.

Two forms of cobalt in fiberglass materials: dimers of Co²⁺_Td in the subsurface layer and isolated Co²⁺_Oh in the bulk.