The study focuses on microstructural evolution in a WC-Co powder mixture during Selective Laser Melting (SLM) and hot isostatic pressing (HIP) processing. This powder mixture contained a 13 ± 0.6% weight fraction of Co binder and WC particles of mean size of 3.0 ± 1.9 μ$\mathrm{m}$. SLM of the mixture produced samples of various densities, depending on the volumetric energy density (VED) applied. High VED levels led to densities of up to 88%. The aspects affected by changes in VED included the pore density as well as the resulting types of phases and the size of WC phase particles. At high VED, the material began to develop cracks due to embrittlement. This had multiple causes: coarsening of $\alpha$-phase (WC), evaporation of $\beta$-phase (Co binder), and precipitation of $\eta$-phase. At low VED levels, pores formed, typically of nonsymmetric shapes, with sizes larger than 500 μ$\mathrm{m}$. Subsequent HIP processing led to an increased density, up to 96% of solid material. Contributions to this increased density were provided by structure transformations, namely, coarsening of $\alpha$-phase by up to 1300% when compared to the powder grain size, and formation of $\eta$-phase. The results provided a basis for steering further research to explore to a greater depth the SLM and HIP processing of selected WC-Co powder mixtures with as yet unused ranges of process parameters.

This paper aimed to investigate the structure and physicochemical and tribological properties of ZnO coatings deposited by ALD on 316L stainless steel for biomedical applications. To obtain ZnO films, diethylzinc (DEZ) and water were used as ALD precursors. Zinc oxide layers were deposited at the same temperature of 200 °C using three types of ALD cycles: 500, 1000 and 1500. The structure and morphology of ZnO coatings were examined using SEM and AFM microscopes. The XRD and GIXRD methods were used for the phase analysis of the obtained coatings. To determine the resistance to pitting corrosion, potentiodynamic investigations and impedance spectroscopy were conducted in a Ringer solution at a temperature of 37 °C. The obtained results showed that the number of ALD cycles had a significant impact on the structure, morphology and corrosion resistance of the ZnO layers. It was found that after increasing the coating thickness of the ZnO on the material, its electrochemical properties determining the corrosion resistance also increased. Moreover, on the basis of the ball-on-plate tribological investigations, we found a significant reduction in the friction coefficient of the samples with the investigated coatings in relation to the noncoated substrates.