Technological innovations and quality control processes within blood supply organizations have significantly improved blood safety for both donors and recipients. Nevertheless, the risk of transfusion-transmitted infection remains non-negligible. Applying a nanoparticular, antibacterial coating at the surface of medical devices is a promising strategy to prevent the spread of infections. In this study, we characterized the antibacterial activity of an SiO₂ nanoparticular coating (i.e., the “Medical Antibacterial and Antiadhesive Coating” [MAAC]) applied on relevant polymeric materials (PM) used in the biomedical field. Electron microscopy revealed a smoother surface for the MAAC-treated PM compared to the reference, suggesting antiadhesive properties. The antibacterial activity was tested against selected Gram-positive and Gram-negative bacteria in accordance with ISO 22196. Bacterial growth was significantly reduced for the MAAC-treated PVC, plasticized PVC, polyurethane and silicone (90–99.999%) in which antibacterial activity of ≥1 log reduction was reached for all bacterial strains tested. Cytotoxicity was evaluated following ISO 10993-5 guidelines and L929 cell viability was calculated at ≥90% in the presence of MAAC. This study demonstrates that the MAAC could prevent bacterial contamination as demonstrated by the ISO 22196 tests, while further work needs to be done to improve the coating processability and effectiveness of more complex matrices.

Platelet concentrates (PCs) are stored at 20–24˚C in a biologically favorable environment that may support bacterial growth. Staphylococcus epidermidis , a typical contaminant, can form biofilms in PCs, complicating detection and increasing the risk of transfusion-transmitted bacterial infections. The material composition and surface texture of PC storage bags may influence biofilm formation. The impact of different PC storage bag materials on S. epidermidis biofilm formation was evaluated using the ISO 4768:2023(E) crystal violet (CV) assay. Four surface conditions were tested: polyvinyl chloride (PVC) plasticized with n-butyryl-tri(n-hexyl)-citrate (BTHC) – both smooth and rough sides, PVC plasticized with tri-(2-ethylhexyl)-trimellitate (TEHTM) and ethylene-vinyl acetate (EVA). Coupons and bags made from each material were used in the experiments. Biofilm-positive S. epidermidis was cultured in tryptic soy broth (TSB), PCs and plasma and added on plastic coupons under static conditions or directly in the bags with agitation. Bacterial enumeration and CV assay were performed on days 2, 5, and 7. In TSB, EVA coupons significantly formed more biofilm than the smooth side of PVC-BTHC or TEHTM over seven days. In PCs, more biofilm formed on the rough side of PVC-BTHC coupons than the smooth side, with no other differences between plastics, suggesting similar biofilm amount across PC bag materials in the presence of platelets. No biofilm was detected on coupons in plasma. Under continuous agitation and reduced oxygen levels, only the rough side of PVC-BTHC showed significant biofilm formation in TSB in PC storage bags over seven days. These findings highlight the need for standardized biofilm testing and suggest that some plastics are more conducive to biofilm formation under static conditions. However, during blood bank storage (i.e., continuous agitation and reduced oxygen levels), biofilm formation is limited, regardless of the platelet bag material, thereby reducing the risk of undetected bacterial contamination.