Contemporary construction faces the need to reduce its negative impact on the environment, prompting designers, investors, and contractors to seek more sustainable materials and technologies. One area of dynamic development is the use of natural fibers as an alternative to conventional, often synthetic, building components. Plant- and animal-based fibers, such as hemp, flax, jute, straw, bamboo, and sheep’s wool, are characterized by low energy consumption in production, renewability, and biodegradability. Their use is in line with the concept of a circular economy and reduces the carbon footprint of buildings. Natural fibers offer a number of beneficial physical and functional properties, including good thermal and acoustic insulation parameters, as well as hygroscopicity, which allows for the regulation of indoor humidity, improving air quality and comfort of use. In recent years, there has also been a renaissance of traditional building techniques, such as straw construction, often combined with modern engineering standards. Their potential is particularly recognized in green and energy-efficient construction. The article provides an overview of the types of natural fibers available for use in construction and analyzes their technical, environmental, and economic properties. It also draws attention to current regulations, standards, and certifications (e.g., LEED, BREEAM) that promote the popularization of these solutions. In light of the analyzed data, the role of natural fibers as a viable alternative supporting the transformation of the construction sector towards sustainable development is considered.

The research described in this article was aimed at determining the influence of hydraulic additives on the foaming process and the stability of the produced geopolymer foams. These foams can be used as insulation materials to replace the currently commonly used insulations such as expanded polystyrene or polyurethane foams. Geopolymers have low thermal conductivity, excellent fire- and heat-resistant properties, and have fairly good mechanical properties. Research on foamed materials shows that they have the highest class of fire resistance; therefore, they are most often used as insulation products in construction. Geopolymer foams were made of aluminosilicate materials (fly ash) and foaming agents (H₂O₂ and Al powder), and the stabilizers were gypsum and portland cement. Additionally, surfactants were also used. It was found that better foaming effects were obtained for H₂O₂—it is a better foaming agent for geopolymers than Al powder. When using a hydraulic additive—a stabilizer in the form of cement—lower densities and better insulation parameters were obtained than when using gypsum. Portland cement is a better stabilizer than gypsum (calcium sulfates), although the effect may change due to the addition of surfactants, for example.

The paper deals with the possibility of using Phase Change Materials (PCM) in concretes and geopolymer composites. The article presents the most important properties of PCM materials, their types, and their characteristics. A review of the latest research results related to their use in geopolymer materials is presented. The benefits of using PCM in building materials include the improvement of thermal comfort inside the building, and also the fact that the additive in the form of PCM reduces thermal gradients and unifies the temperature inside the concrete mix, which can reduce the risk of cracking. The paper also presents a critical analysis related to the feasibility of mass scale implementations of such composites. It was found that the use of PCM in sustainable construction is necessary and inevitable, and will bring a number of benefits, but it still requires large financial resources and time for more comprehensive research. Despite the fact that PCM materials have been known for many years, it is necessary to refine their form to very stable phases that can be used in general construction as well as to develop them in a cost-effective form. The selection of these materials should also be based on the knowledge of the matrix material.

Geopolymers are binder materials that are produced by a chemical reaction between silica or aluminum compounds with an alkaline activating solution. Foamed geopolymer materials are increasingly being cited as a viable alternative to popular organic insulation materials. Since the foaming process of geopolymers is difficult to control, and any achievements in improving the performance of such materials are extremely beneficial, this paper presents the effect of the addition of basalt powder on the properties of foamed geopolymers. This paper presents the results of physicochemical studies of fly ash and basalt, as well as mechanical properties, thermal properties, and structure analysis of the finished foams. The scope of the tests included density tests, compressive strength tests, tests of the thermal conductivity coefficient using a plating apparatus, as well as microstructure tests through observations using light and scanning microscopy. Ground basalt was introduced in amounts ranging from 0 to 20% by mass. It was observed that the addition of basalt powder contributes to a reduction in and spheroidization of pores, which directly affect the density and pore morphology of the materials tested. The highest density of 357.3 kg/m³ was characterized by samples with a 5 wt.% basalt powder addition. Their density was 14% higher than the reference sample without basalt powder addition. Samples with 20 wt.% basalt addition had the lowest density, and the density averaged 307.4 kg/m³. Additionally, for the sample containing 5 wt.% basalt powder, the compressive strength exceeded 1.4 MPa, and the thermal conductivity coefficient was 0.1108 W/m × K. The effect of basalt powder in geopolymer foams can vary depending on many factors, such as its chemical composition, grain size, content, and physical properties. The addition of basalt above 10% causes a decrease in the significant properties of the geopolymer.

Geopolymer concretes can be a viable alternative to conventional Portland cement-based materials. In their design, it is important to maintain an appropriate liquid-to-solid ratio (L/S), which affects several properties, such as the compressive strength, water absorption, and frost resistance. The objective of this paper is to analyze the influence of the fly-ash and metakaolin precursor types for three different L/S ratios: 0.30, 0.35, and 0.45. The results of the physical and mechanical properties, including the apparent density and compressive strength, as well the durability parameters, including frost resistance and water penetration depth, are presented in this paper. It was found that as the L/S ratio decreased, the average compressive strength increased for all materials. After freeze–thaw cycles, decreases in the compressive strength properties were observed for all types of materials—metakaolin- and fly ash-based—irrespective of the L/S ratio. Moreover, the frost resistance of geopolymers increased with the increase in the L/S ratio. The printability of the mixes was also verified in order to confirm the application of the developed materials to additive manufacturing processes.

New restrictions on carbon dioxide emissions and electricity consumption are currently being introduced around the world. Innovative solutions are being adopted in many countries to reduce CO₂ emissions and material and energy consumption. The present work is related to the study of innovative binders based on geopolymers for the production of layered building envelopes. The binders are reinforced with composite bars and containing fibers of natural origin. The natural materials used to produce the samples are completely biodegradable. A 10-mol sodium hydroxide solution with an aqueous solution of sodium silicate was used for alkaline activation of geopolymers. The purpose of the study was to compare and determine the insulating properties of natural fiber-based materials such as coconut mat, jute felt, hemp felt, flax felt, flax wool, hemp wool, flax-jute wool, and to determine the effect of these materials on geopolymer composites, in which 4 layers of natural insulating materials were used, and the composites were reinforced by fiberglass bars. The publication presents the results of physicochemical studies of geopolymerization precursors and natural insulating materials, studies of thermal properties of fibers, mats, felts and wools, morphology of fiber structure and texture, as well as physical and thermal properties of finished multi-layer partitions. The results indicate the great potential of these materials in prefabrication and structural-insulation applications. The fabricated composites using 4 layers of natural fibers showed improved thermal conductivity by as much as 40% (reduced thermal conductivity from 1.36 W/m × K to about 0.8 W/m × K). The work may have future applications in energy-saving and low-carbon construction.