Thermal simulation equipment (TSE) was recently developed to simulate the solidification process in the industrial continuous casting of slab. The grain growth, solid-liquid interface movement, and columnar-to-equiaxed transition (CET) in the continuous casting process can be reproduced using this equipment. The current study is focused on the effects of different cooling rates and superheat conditions on the grain growth in the solidification process of chromium-saving ferritic stainless steel (B425). The temperature distribution and microstructure evolution are simulated by a Cellular Automaton-Finite Element (CAFE) model. The experimental results demonstrate that the temperature gradient and the grain growth rate of the sample can be effectively controlled by the equipment. It is observed from optical micrographs of the microstructure that the average equiaxed grain ratio increases when the superheat temperature decreases. The average equiaxed grain ratio is approximately 26% and 42% under superheat conditions of 40 °C and 30 °C, respectively, and no apparent columnar grain generation in the samples occurs under superheat conditions of 10 °C and 20 °C, as the result of a large thermal resistance at the copper-sample interface and low superheat inside the sample. A lower cooling rate results in a higher equiaxed crystal ratio in the sample. As the cooling rate decreases, the equiaxed crystal ratio becomes 14%, 23%, and 42%. Comparing the simulation results with the experimental observations, a reasonable qualitative agreement is achieved for the chilled layer thickness, grain morphology, and CET in the sample. Thus, the CAFE model in the current study can accurately predict the grain growth under different superheating and cooling rate conditions.

It is high of commercial importance to generate the grain refinement in alloys during solidification by means of electromagnetic fields. Two typical patterns of electromagnetic fields, pulsed electric currents (ECP) and traveling magnetic field (TMF), are frequently employed to produce the finer equiaxed grains in solidifying alloys. Various mechanisms were proposed to understand the grain refinement in alloys caused by ECP and TMF. In this paper, a comparative study is carried out in the same solidification regime to investigate the grain refinement of Al-7 wt. %Si alloy driven by ECP and TMF. Experimental results show that the application of ECP or TMF can cause the same grain refinement occurrence period, during which the refinement of primary Al continuously occurs. In addition, the related grain refinement mechanisms are reviewed and discussed, which shows the most likely one caused by ECP and TMF is the promoted dendrite fragmentation as the result of the ECP-induced or TMF-induced forced flow. It suggests that the same grain refinement process in alloys is provoked when ECP and TMF are applied in the same solidification regime, respectively.