A new copolymer has been studied, which is formed by Poly(2-methoxy-5-(2-ethyl-hexyloxy)-1,4-phenylene-vinylene) (MEH-PPV) and poly(3-hexylthiophene) (P3HT). The choice of these π-conjugated polymers was based on their semiconductor characters and their great applicability in electronic organic devices. The structure and vibrational and optoelectronic properties were simulated by calculations based on DFT, TD-DFT, and ZINDO. This material shows original and unique properties compared to the basic homopolymers. Thus, the obtained results reveal that this copolymer can be mixed with the (6,6)-phenyl C61 butyric acid methyl ester (PCBM) to give existence to a new composite that can be used as an active layer for an organic solar cell.

The current work is driven by applying circular principles, and it investigated the potential recyclability of polybutylene succinate (PBS) containing brewer’s spent grain filler (BSGF, 30 wt%) in comparison to the recyclability of pure PBS. PBS is much more stable than the PBS/BSGF composite during processing cycles. Typically, thermomechanical degradation induces radical formation and branching of the macromolecular chain in PBS. Furthermore, PBS becomes less hydrophilic (by 53%, reaching 84°, approaching the 90° threshold), and its surface roughness increases by about 38% after five processing cycles. BSGF increases the viscosity of the melt, especially at low frequencies, and stabilizes the melt in the PBS/BSGF, which has lower torque variations during processing compared to pure PBS. Furthermore, BSGF in r-PBS/BSGF increases both hydrophilicity (by about 15%, from 75° to 64°) and surface roughness (by about 17%) after five processing cycles of the solid bio-composite and limits the formation of carboxylic groups during thermomechanical degradation. PBS is recyclable five times because it maintains its properties unchanged during extrusion cycles. At least two reprocessing steps are required for PBS/BSGF to obtain an optimal dispersion of BSGF, which can be re-extruded approximately three times. PBS/BSGF after four and five extrusion steps shows increased rigidity (E_t PBS/BSGF > E_t PBS) and reduced ductility (ε_b PBS/BSGF < ε_bt PBS), which could limit the recyclability of the PBS-based composite.