Various industrial activities release heavy metal ions into the environment, which represent one of the major toxic pollutants owing to their severe effects on the environment, humans, and all living species. Despite several technological advances and breakthroughs, wastewater treatment remains a critical global issue. Traditional techniques are dedicated to extracting heavy metal ions from diverse wastewater origins, encompassing coagulation/flocculation, precipitation, flotation, and ion exchange. Their cost, side toxicity, or ineffectiveness often limit their large-scale use. Due to their adaptable design, simple operation, and reasonable cost, membrane filtration and adsorption have proven their efficiency in removing metals from wastewater. Recently, adsorption-based filters have appeared promising in treating water. Within this range, filters incorporating natural, synthetic, or hybrid adsorbents present an appealing alternative to conventional approaches. This review aims to list and describe the conventional and advanced wastewater treatment methods by comparing their efficiency, cost, and environmental impact. Adsorption-based filters were highlighted due to the significant advantages they can provide.

The accumulation of heavy metals and dyes in wastewater is a persistent environmental threat with serious hazards consequences affecting all living organisms. Citrus Sinensis peel and its activated carbon particles effectively remove Cu( ii ), Cd( ii ), and MB from water.

Polyaniline-assisted deposition of PbS is carried out on antimony tin oxide (ATO) glass for ATO/PANI/PbS composite formation. The deposition of PbS was carried out inside and outside the polymer chains using the ionic adsorption deposition process. Various analyses were conducted to confirm the chemical structure and morphological, optical, and electrical properties of the resulting composite. TEM and SEM analyses demonstrated the spherical shape of PbS particles inside and outside the PANI network with more dark or white color, respectively. Moreover, the ImageJ program confirmed the composite formation. The XRD characterization showed the shifts in the PANI peaks after the composite formation with the appearance of a new additional peak related to PbS nanoparticles. The optical analyses were massively enhanced after the composite formation with more broadening in the Vis region at 630 nm, in which there was more enhancement in the bandgap that reached 1.5 eV. The electrode application in the H₂ generation process was carried out from wastewater (sewage water, third treatment) without any additional sacrificing agent. The electrode responded well to light, where the current density ([ ]) changed from 10^-6 to 0.13 mA.cm^-2 under dark and light, respectively. The electrode had high reproducibility and stability. The numbers of generated H₂ moles were 0.1 mmol/cm².h. The produced [ ] and [ ] were 7.3 kJ/mol and 273.4 J/mol.K, respectively. Finally, the mechanism explains the H₂ generation reaction using three-electrode cell.

The heavy metals pollutants resulting from industrial wastewater are a major environmental problem due to their toxicity and non-biodegradability. Their removal became a trending environmental subject. The preparation of low-cost and eco-friendly adsorbents for industrial wastewater treatment has...

This study describes the preparation and characterization of glass/poly-3-methyl aniline (P3MA)/PbS quantum dot (QD) optoelectronic photodetector to detect and sense the light in broad spectral regions of UV, Vis, and NIR. This work is carried out to solve the drawbacks of other studs that prepare detectors in just one or two optical regions. Previous studies have used high-priced techniques. The deposition of P3MA on the glass surface was carried out by in situ oxidation process. Then, this polymer film was used to assist the deposition of PbS-QD particles through the ionic adsorption deposition method. The latter was performed using four different concentrations of Pb(NO₃)₂ solution (0.01, 0.03, 0.05, and 0.07 M) to form four P3MA/PbS composites: I, II, III, and IV, respectively. The chemical structure, morphologies, and electrical and optical properties of these composites were determined using different analytical tools. The SEM confirmed the formation of spherical QD particles of PbS on the P3MA surface. The TEM analysis showed that the composite has an average size of 5 nm, with the interatomic distances of 0.4 nm. Furthermore, the optical band gap values were 1.53, 1.52, 1.50, and 1.51 eV, respectively. The optoelectronic device could detect and sense light from 390 to 636 nm under various optical wavelengths. The produced current density ([ ]) values decreased from 0.029 mA.cm^-2 at 390 nm to 0.022 mA.cm^-2 at 500 nm and then increased until 0.024 mA.cm^-2 at 636 nm. The light sensing was determined through the photoresponsivity ([ ]) and detectivity ([ ]) parameters, in which the photodetector has [ ] and [ ] values of 0.29 mA.cm^-2 and [ ] Jones, respectively. Finally, a simple mechanism was proposed to explain the light sensing through the prepared optoelectronic device. Soon, our team works on the industrial applications of this optoelectronic device in the industry field related to the great optoelectronic device technical properties and its low cost and easy preparation.