Vacuum environments provide challenging conditions for tribological systems. MoS₂ is one of the materials commonly known to provide low friction for both ambient and vacuum conditions. However, it also exhibits poor wear resistance and low ability to withstand higher contact pressures. In search of wear-resistant alternatives, superhard hydrogen-free tetrahedral amorphous carbon coatings (ta-C) are explored in this study. Although known to have excellent friction and wear properties in ambient atmospheres, their vacuum performance is limited when self-paired and with steel. In this study, the influence of the paired material on the friction behavior of ta-C is studied using counterbodies made from brass, bronze, copper, silicon carbide, and aluminum oxide, as well as from steel and ta-C coatings as reference materials. Brass was found to be the most promising counterbody material and was further tested in direct comparison to steel, as well as in long-term performance experiments. It was shown that the brass/ta-C friction pair exhibits low friction (µ < 0.1) and high wear in the short term, irrespective of ambient pressure, whereas in the long term, the friction coefficient increases due to a change in the wear mechanism. Al₂O₃ was identified as another promising sliding partner against ta-C, with a higher friction coefficient than that of brass (µ = 0.3), but considerably lower wear. All other pairings exhibited high friction, high wear, or both.

Vacuum and air atmospheres impose very different requirements on tribological-loaded contacts, which usually require different surface materials. While hard tetrahedral amorphous carbon (ta-C) coatings provide good tribological properties in air, soft coatings such as molybdenum disulfide (MoS2) work well in a vacuum. Tribological performance in the respective other environment, however, is poor. In this work, the combination of laser microstructured (direct laser interference patterning) steel substrates and the deposition of ta-C and MoSx coatings with vacuum arc evaporation (LaserArc™) was studied, resulting in steel/DLIP, steel/DLIP/ta-C, steel/DLIP/MoSx, steel/DLIP/ta-C/MoSx, and steel/MoSx surface combinations. The tribological properties were studied using a ball-on-disk tribometer with a steel ball counter body in air and in a vacuum (p < 5 × 10⁻⁷ mbar). The type of the topmost coating governed their tribological properties in the respective atmosphere, and no general beneficial influence of the microstructure was found. However, steel/DLIP/ta-C/MoSx performed best in both conditions and endured the highest contact pressure, which is attributed to the mechanical support of the ta-C coating and MoSx reservoir in the remaining structure, as evidenced by Raman spectroscopy. The findings suggest that such combination allows for surfaces bearing a high load capacity that can be applied in both a vacuum and in air, for example, in multi-use space applications.