In this study, both the plasma process of filtered laser-arc evaporation and the resulting properties of tetrahedral amorphous carbon coatings are investigated. The energy distribution of the plasma species and the arc spot dynamics during the arc evaporation are described. Different ta-C coatings are synthesized by varying the bias pulse time and temperature during deposition. An increase in hardness was observed with the increased overlapping of the bias and arc pulse times. External heating resulted in a significant loss of hardness. A strong discrepancy between the in-plane properties and the properties in the film normal direction was detected specifically for a medium temperature of 120 °C during deposition. Investigations using electron microscopy revealed that this strong anisotropy can be explained by the formation of nanocrystalline graphite areas and their orientation toward the film’s normal direction. This novel coating type differs from standard amorphous a-C and ta-C coatings and offers new possibilities for superior mechanical behavior due to its combination of a high hardness and low in-plane Young’s Modulus.

Coatings used in tribological applications often exhibit high hardness and stiffness to achieve high wear resistance. One coating characterization method frequently used is nanoindentation which allows the determination of indentation hardness and indentation modulus among other material properties. The indentation modulus describes the elastic surface behavior during indentation and is, among hardness, a direct indicator for wear resistance. To obtain the true indentation modulus of a coating, it must be measured with varying loads and then extrapolated to zero load. Current recommendation of the standard ISO 14577-4:2016 is a linear extrapolation which fits poorly for nonlinear curves. Such nonlinear curves are commonly found for high hardness mismatches between coating and substrate, for example, superhard tetrahedral amorphous carbon coatings (ta-C) on a steel substrate. In this study, we present a new empirical fit model, henceforth named sigmoid. This fit model is compared to several existing fit models described in the literature using a large number of nanoindentation measurements on ta-C coatings with wide ranges of indentation modulus and coating thickness. This is done by employing a user-independent and model agnostic fitting methodology. It is shown that the sigmoid model outperforms all other models in the combination of goodness of fit and stability of fit. Furthermore, we demonstrate that the sigmoid model’s fit parameter directly correlates with coating thickness and thus allows for a new approach of determining ta-C coating thickness from nanoindentation.

Vacuum environments provide challenging conditions for tribological systems. MoS₂ is one of the materials commonly known to provide low friction for both ambient and vacuum conditions. However, it also exhibits poor wear resistance and low ability to withstand higher contact pressures. In search of wear-resistant alternatives, superhard hydrogen-free tetrahedral amorphous carbon coatings (ta-C) are explored in this study. Although known to have excellent friction and wear properties in ambient atmospheres, their vacuum performance is limited when self-paired and with steel. In this study, the influence of the paired material on the friction behavior of ta-C is studied using counterbodies made from brass, bronze, copper, silicon carbide, and aluminum oxide, as well as from steel and ta-C coatings as reference materials. Brass was found to be the most promising counterbody material and was further tested in direct comparison to steel, as well as in long-term performance experiments. It was shown that the brass/ta-C friction pair exhibits low friction (µ < 0.1) and high wear in the short term, irrespective of ambient pressure, whereas in the long term, the friction coefficient increases due to a change in the wear mechanism. Al₂O₃ was identified as another promising sliding partner against ta-C, with a higher friction coefficient than that of brass (µ = 0.3), but considerably lower wear. All other pairings exhibited high friction, high wear, or both.

Vacuum and air atmospheres impose very different requirements on tribological-loaded contacts, which usually require different surface materials. While hard tetrahedral amorphous carbon (ta-C) coatings provide good tribological properties in air, soft coatings such as molybdenum disulfide (MoS2) work well in a vacuum. Tribological performance in the respective other environment, however, is poor. In this work, the combination of laser microstructured (direct laser interference patterning) steel substrates and the deposition of ta-C and MoSx coatings with vacuum arc evaporation (LaserArc™) was studied, resulting in steel/DLIP, steel/DLIP/ta-C, steel/DLIP/MoSx, steel/DLIP/ta-C/MoSx, and steel/MoSx surface combinations. The tribological properties were studied using a ball-on-disk tribometer with a steel ball counter body in air and in a vacuum (p < 5 × 10⁻⁷ mbar). The type of the topmost coating governed their tribological properties in the respective atmosphere, and no general beneficial influence of the microstructure was found. However, steel/DLIP/ta-C/MoSx performed best in both conditions and endured the highest contact pressure, which is attributed to the mechanical support of the ta-C coating and MoSx reservoir in the remaining structure, as evidenced by Raman spectroscopy. The findings suggest that such combination allows for surfaces bearing a high load capacity that can be applied in both a vacuum and in air, for example, in multi-use space applications.

Triboscopy focuses on the analysis of the temporal evolution of a tribological system, combining local and time-resolved information, most commonly the evolution of friction. In this work, this technique is applied on measurements, which were carried out with a custom-built ultra-high vacuum tribometer in ball-on-disc configuration. Based on these experiments, an extended classification to distinguish different triboscopic features is suggested, depending on the persistence in both track position and time: Uniform, Global, Local, and Sporadic. Further, a filter technique for quantifying triboscopic data regarding this classification is introduced. The new and improved triboscopic techniques are applied to various dry friction measurements of hydrogen-free carbon coatings under varying humidity and pressure. The resulting specific triboscopic features are correlated to wear phenomena, such as counter body coating abrasion, inhomogeneities in the wear track, non-uniform track wear, stick-slip and debris in the contact area, demonstrating the increased analysis and monitoring capabilities when compared to conventional friction curves and wear track images.