Impact of stabilisers on the catalytic performance of supported Au colloidal nanoparticles for the liquid phase oxidation of glucose to glucaric acid.

Supported on activated carbon gold colloidal nanoparticles have been prepared in the presence of the stabilizing polymer PVA and PVP (polyvinylalcohol, polyvinylpyrrolidone). The effect of the polymer to the Au weight ratio was investigated, for synthesizing gold nanoparticles with different particle size and particle size distribution. By varying the polymer/Au wt/wt ratio, gold nanoparticles with mean diameters from 3 to 8 nm were synthesized. The synthesized Au catalysts were studied in the liquid phase oxidation of 1,6-hexanediol (HDO) to adipic acid under base and base-free conditions. A range of experimental parameters were varied for the optimization of reaction conditions and the most promising Au catalysts were further evaluated in terms of catalytic performance. We demonstrated that the influence of choice of polymer, tuning the polymer to Au weight ratio, HDO to Au molar ratio, and use of basic conditions have an important influence in terms of catalytic activity and selectivity to adipic acid. The highest yield to adipic acid was obtained using Au-PVA catalysts (40% at 110 °C under base free conditions), however, at low HDO to Au molar ratio and lower carbon balance (70–80%). On the contrary, at higher HDO to Au molar ratio, and under basic conditions, the yield was in the range of 18–20% with a significant improvement in terms of carbon balance (88–100%).

Different series of Au on carbon catalysts were prepared via sol-immobilization to investigate the role of polymers (polyvinylpyrrolidone PVP, polyethylene glycol PEG and polyvinyl alcohol PVA), employed as gold nanoparticle (NP) stabilizers, on catalyst properties and on catalytic activity. The synthesized materials were widely characterized with several techniques (DLS, XRD, TEM and XPS) and used as catalysts in the 5-hydroxymethylfurfural (HMF) oxidation to produce 2,5-furandicarboxylic acid (FDCA). The obtained results clearly demonstrated the PVA leading to the formation of smaller and more active NPs. On the contrary, polyethylene glycol was shown to affect gold exposure and, as a consequence, to reduce the catalyst activity due to steric effects while PVP-based catalysts presented bigger and more covered Au NPs. The investigation on the reusability of the catalysts demonstrated the presence of a significant deactivation on all prepared materials, but the presence of higher amounts of polymer seems to have a positive effect on catalyst stability even if associated with lower reactivity. Computational studies have provided interesting information on the NP-polymer interactions and consequently on the catalytic activities.