Functional magnesium oxide-lignin hybrid materials were obtained via mechanical grinding. Their particle shape and size as well as physicochemical properties were characterized. MgO-lignin materials with biocomponent content (between 20% and 80% amount of total weight of filler) were used as a partially bio-structured modifier of low density polyethylene. The composites with 5% by weight of dual fillers and polyethylene grafted with maleic anhydride were compounded in a twin screw extruder working in co-rotating mode. The prepared blends were cast extruded using a single screw extruder and laboratory cast line. The properties of the obtained films were verified in case of their weldability. The seal strength as well as shear test and tear strength of the welded sheets were examined. The results showed that the shortest equivalent time required to perform correct weld occurred in the system, where the highest amount of lignin was used in hybrid filler MgO-L (1:5 w/w). From mechanical tests of welds, a sharp increase in ultimate seal force was noticed for almost all compositions with lignin, especially where MgO was coupled with a high lignin content. For those composition seal open force raised up to 37.0 N, from the value of 23.6 N, achieved for neat low density polyethylene (LDPE). Tear strength of weld sheets confirmed once more that LDPE composition with MgO-L (1:5 w/w) achieved the highest ultimate force with its value of 71.5 N, and it was ~20.0 N higher than in the case of neat LDPE.

Hydroxyapatite is a widely used material used for the bioactivation of an implant’s surface. A promising hydroxyapatite coating approach is the kinetic deposition of powder particles. The possibility of solid-state deposition improvement through the merging of Aerosol Deposition and Low Pressure Cold Spraying techniques is a promising prospect for improving the deposition efficiency and the quality of coatings. The objective of the paper is to study the possibilities of hydroxyapatite coating structure modification through changes in the coating process and post-heat treatment. The novel Aerosol Cold Spraying system joining Low Pressure Cold Spraying and Aerosol Deposition was used for the deposition of coatings. The coating’s post-processing was conducted using two techniques: Spark Plasma Sintering and Pressureless Sintering. The coating’s structure was examined using scanning, transmission, and light microscopy, and X-ray diffraction. Substrate–coating bond strength was assessed using a tensile test. Homogenous buildup using Aerosol Cold Spraying of hydroxyapatite was achieved. Various pores and microcracks were visible in the sprayed coatings. The deposition process and the thermal post-processing did not lead to significant degradation of the hydroxyapatite phase. As a result of the Spark Plasma Sintering and Pressureless Sintering at 800 °C, an increase in tensile adhesion bond strength and crystal size was obtained.

The presented study describes the application of lignin-based dual component fillers into low-density polyethylene (LDPE) and an examination of their selected properties. The main experimental procedure was focused on the preparation of thin sheet films using polyethylene and its composites with 5% by wt. of fillers: MgO, MgO-lignin dual phase systems with varying amounts of lignin and pristine lignin. Analysis of morphology revealed that elongated voids appeared in the structure for hybrid filler with a higher content of lignin (min. 50% by wt. of lignin versus MgO) and also for pristine lignin. Moreover, the prepared sheets were subjected to the thermoforming process by using the positive forming method (male mold). The thermoforming ability of all composites was evaluated by means of a comparison of wall thickness distribution on thermoformed shapes. The most noticeable percentage of wall thinning occurred for films which consisted of LDPE/MgO-lignin (5:1 wt./wt.) composite. In contrast, the best material arrangement and the highest mean percentage wall thickness were observed in the case of the shape formed with LDPE/MgO-lignin (1:5 wt./wt.). In addition, as part of research studies, the measurements of the contact angle have been conducted. The analysed LDPE films, in particular LDPE/MgO-L, have been recognized as materials with high wettability.

High-temperature conditions are harmful for carbon nanotube-based (CNT-based) composites, as CNTs are susceptible to oxidation. On the other hand, adding CNTs to ceramics with low electrical conductivity, such as 3YSZ, is beneficial because it allows the production of complex-shaped samples with spark plasma sintering (SPS). A shielding coating system may be applied to prevent CNT oxidation. In this work, the 8YSZ (yttria-stabilized zirconia) thermal shielding coating system was deposited by aerosol deposition (AD) to improve the composite’s resistance to CNT degradation without the use of bond-coat sublayers. Additionally, the influence of the annealing process on the mechanical properties and microstructure of the composite was evaluated by nanoindentation, scratch tests, scanning electron microscopy (SEM), X-ray diffraction (XRD), flame tests, and light microscopy (LM). Annealing at 1200 °C was the optimal temperature for heat treatment, improving the coating’s mechanical strength (the first critical load increased from 0.84 N to 3.69 N) and promoting diffusion bonding between the compacted powder particles and the substrate. The deposited coating of 8YSZ increased the composite’s thermal resistance by reducing the substrate’s heating rate and preventing the oxidation of CNTs.

The MAX phases, a group of layered ternary carbides and nitrides, have been known since the 1960s and have attracted significant interest for their unique properties that combine the advantages of ceramics and metals. One of the most cost-effective methods for fabricating MAX phases is spark plasma sintering (FAST|SPS), which provides reasonable control over phase content and short processing times due to the rapid heating and cooling rates. To improve the scalability of FAST|SPS, high-energy ball milling (HEBM) can be used to pre-alloy the precursor powders and initiate the exothermic reaction before sintering. However, scaling up synthesis poses challenges related to thermal homogeneity and MAX phase purity. This study uses thermal modeling to analyze how FAST|SPS parameters and sintering tool design influence the large-scale synthesis of powder materials. Experiments verified the modeling results. The 800g batch of Ti3AlC2 MAX phase with uniform composition, was sintered in a single FAST|SPS cycle.