During ultrasonic testing of resistance spot welds in real time, the probe sends the sound waves through the thickness of the copper electrode cap into the materials being welded. Characteristics of the reflected waves from the weld interfaces allow a reliable decision to be made on the quality of the joint. Transmission of high frequency sound waves through the relatively thick copper welding cap cause the signal to be greatly attenuated due to grain scattering. For this reason, close monitoring of the copper cap properties prior to installation is essential for adequate performance. Finding copper alloys with a small average grain size is essential in order to minimize the attenuating effects. The conducted backscatter and attenuation experiments indicate correlation between the ultrasonically measured parameters and the optically found copper grain size. This correlation suggests that the attenuation or backscatter technique could be used alone in order to validate the proper copper alloy to be used in spot weld probes. Using nondestructive testing techniques for this purpose greatly reduces the time and cost involved compared to optical techniques.

This paper aimed to study the correlation between Real Time Integrated Weld Analyzer measurements and peel test results. The experiment involved study of weld nuggets for different combinations of sheet thicknesses, welding time and current of mild steel samples. The intent was to assess the potential use of a real time integrated ultrasonic system in the industrial environment allowing nondestructive evaluation of 100% of the spot welds produced. The results showed high correlation between nugget penetration into the sheets and nugget size measured ultrasonically and destructively, for all evaluated parameters.

Hydroxyapatite is a widely used material used for the bioactivation of an implant’s surface. A promising hydroxyapatite coating approach is the kinetic deposition of powder particles. The possibility of solid-state deposition improvement through the merging of Aerosol Deposition and Low Pressure Cold Spraying techniques is a promising prospect for improving the deposition efficiency and the quality of coatings. The objective of the paper is to study the possibilities of hydroxyapatite coating structure modification through changes in the coating process and post-heat treatment. The novel Aerosol Cold Spraying system joining Low Pressure Cold Spraying and Aerosol Deposition was used for the deposition of coatings. The coating’s post-processing was conducted using two techniques: Spark Plasma Sintering and Pressureless Sintering. The coating’s structure was examined using scanning, transmission, and light microscopy, and X-ray diffraction. Substrate–coating bond strength was assessed using a tensile test. Homogenous buildup using Aerosol Cold Spraying of hydroxyapatite was achieved. Various pores and microcracks were visible in the sprayed coatings. The deposition process and the thermal post-processing did not lead to significant degradation of the hydroxyapatite phase. As a result of the Spark Plasma Sintering and Pressureless Sintering at 800 °C, an increase in tensile adhesion bond strength and crystal size was obtained.

Thermography is a powerful tool for non-destructive testing of a wide range of materials. Thermography has a number of approaches differing in both experiment setup and the way the collected data are processed. Among such approaches is the Principal Component Thermography (PCT) method, which is based on the statistical processing of raw thermal images collected by thermal camera. The processed images (principal components or empirical orthogonal functions) form an orthonormal basis, and often look like a superposition of all possible structural features found in the object under inspection—i.e., surface heating non-uniformity, internal defects and material structure. At the same time, from practical point of view it is desirable to have images representing independent structural features. The work presented in this paper proposes an approach for separation of independent image patterns (archetypes) from a set of principal component images. The approach is demonstrated in the application of inspection of composite materials as well as the non-invasive analysis of works of art.

Yttrium-stabilized zirconia thermal barrier coatings (TBCs) of combustion chambers and piston crowns are used most frequently to increase the chamber temperature and the internal combustion engine efficiency. The development of multilayer metal matrix composite coating is of great importance to diminish the ceramic thermal barrier coating’s brittleness and susceptibility to degradation providing the similar thermal insulation. Our group is developing multilayer TBCs based on intermetallic (Fe-Al) compounds combined with alternating zirconia-based layers made by low-pressure cold spraying (LPCS) and sintering. The Fe-Al intermetallic phase was synthesized during reaction sintering of stainless steel and Al particles in the powder layer previously obtained by cold spraying. A double-nozzle low-pressure cold-spraying gun was used to deposit two layers (stainless steel and Al-YSZ) per one track. The effect of the breaking of the brittle ZrO₂ particles due to impingement with the substrate results in the formation of a relatively homogeneous structure with ZrO₂ particle size of 3–10 μm. Cold-spray deposition of additional Cu-Ni-Graphene catalytic layers on the TBCs is developed to improve performance and emissions of engines. The microstructure, thermal conductivity, thermal shock behavior and microhardness of TBCs were examined and discussed.