This work presents the results of the electron-beam welding of commercially pure α-Ti (CP-Ti) and Ti6Al4V (Ti64) alloys. The structure and mechanical properties of the formed welded joints were examined as a function of the power of the electron beam. The beam power was set to P₁ = 2100 W, P₂ = 1500 W, and P₃ = 900 W, respectively. X-ray diffraction (XRD) experiments were performed in order to investigate the phase composition of the fabricated welded joints. The microstructure was examined by both optical microscopy, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDX). The mechanical properties of the formed joints were studied using tensile test experiments and microhardness experiments. The results of the experiments were discussed concerning the influence of the beam power on the microstructure and the mechanical properties of the weld joints. Furthermore, the practical applicability of the present method for the welding of α-Ti and Ti64 was also discussed.

In this study, we present the results of the effect of duplex surface modification of 304-L stainless steel substrates by an electron-beam treatment (EBT) and subsequent deposition of diamond-like carbon coatings on the surface roughness and corrosion behavior. During the EBT process, the beam power was varied from 1000 to 1500 W. The successful deposition of the DLC coatings was confirmed by FTIR and Raman spectroscopy experiments. The results showed a presence of C–O, C=N, graphite-like sp², and mixed sp²-sp³ C–C bond vibrations. The surface topography was studied by atomic force microscopy. The rise in the beam power leads to a decrease in the surface roughness of the deposited DLC coatings. The studies on the corrosion resistance of the samples have been performed using three electrochemical techniques: open circuit potential (OCP), cyclic voltammetry (polarization measurements), and non-destructive electrochemical impedance spectroscopy (EIS). The measured corrosion potentials suggest that these samples are corrosion-resistant even in a medium, containing corrosive agents such as chloride ions. It can be concluded that the most corrosion-resistant specimen is DLC coating deposited on electron-beam-treated 304-L SS substrate by a beam power of 1500 W.

This work presents the results of an investigation into the influence of beam offset on the structure and mechanical properties of electron-beam-welded joints between Ti6Al4V and Al6082-T6 alloys. The experimental procedure involved the use of specific technological conditions: an accelerating voltage of 60 kV, an electron beam current of 35 mA, a specimen motion speed of 10 mm/s, and a beam offset of 0.5 mm towards both alloys, as well as welding without an offset. The phase composition of the joints was analyzed using X-ray diffraction (XRD). The microstructure and chemical composition of the seams were studied by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). The results obtained for the structure of the joints show that the beam offset has a significant influence on the structure. The microhardness was studied by means of the Vickers method. The results for the microstructure showed that the welding procedure without offset and with an offset towards the Ti alloy leads to inhomogeneous welded joints with a significant amount of intermetallics. The offset towards the Al alloy leads to the formation of a narrow area of TiAl₃ phase. The measured microhardness corresponds to the increased amount of intermetallics in the case of offset towards the Ti alloy, with which the highest values were presented (about 58% higher than with Ti6Al4V plate). The results obtained for tensile properties show that the offset to the Al6082-T6 alloy leads to the highest values of tensile strength (TS) and yield strength (YS), which are twice higher than in welding without offsetting of the electron beam.

In the current paper, the correlation between the physical size of additively built wire arc specimens and their structure and properties is studied. For the purpose of this work, two oval shaped specimens of different lengths were manufactured under the same technological conditions. The specimens have a length of 200 mm and 400 mm and will be referred to as L200 and L400. The microstructure of the samples was studied using X-ray diffraction analysis (XRD), optical microscopy, and scanning electron microscopy (SEM). The microhardness, yield strength (YS), and ultimate tensile strength (UTS) were determined and their correlation with the technological conditions of specimen build-up was clarified. The results of the carried out experiments indicated that the crystallographic structure of both specimens is similar. The scanning electron microscopy images show a higher concentration of irregularly shaped micro-pores formed near the edge of the αAl grains in the structure of the L400 specimen compared to the L200 one. An increase in the size of the αAl solid solution grains in the case of the L200 specimen towards its top section was noticed using optical microscopy. A slightly lower magnitude change was noticed concerning the L400 specimen. The increase in the size of the aluminum crystals was determined to be the increasing interpass temperature. Due to the much smaller thermal dissipation capacity of the smaller specimen, the interpass temperature of the same increased faster compared to the larger specimen. All of the above-mentioned factors led to a decrease in the microhardness of the specimens at higher stages of build-up. Since the specimens were deposited using similar layer deposition conditions, the resultant YS and UTS data are also highly comparable.

In this study, we present the results from electron-beam welding operations applied on copper and Al6082T6 aluminum alloys. The influence of beam-scanning geometries on the structure and mechanical properties of the welded joint is studied. The experiments were conducted using a circle oscillation mode with an oscillation radius of 0.1 mm and 0.2 mm. The beam deflection was set to 0.4 mm with respect to the side of the aluminum alloy, and the beam power was set at 2700 W. The phase composition of the obtained welded joints was studied by X-ray diffraction (XRD). Scanning electron microscopy (SEM) was used for the investigation of the microstructure of the joints. The chemical composition was investigated by using energy-dispersive X-ray spectroscopy (EDX). The mechanical properties were studied by micro-hardness investigations. The fusion zone of the weld seam contains three phases—an aluminum matrix, an ordered solid solution of copper and aluminum in the form of CuAl₂, and pure copper. Electron beam-scanning geometries have significant influences on the structure of the weld. Increasing the beam oscillation’s radius leads to a decrease in intermetallic phases and improves homogeneity. The measured microhardness values in the fusion zone are much higher than the ones measured in the base metals due to the formation of intermetallic phases. The microhardness of the weld joint formed using an oscillation radius of 0.2 mm was much lower compared to the one formed using an oscillation radius of 0.1 mm.

For the purpose of this research, single track details were manufactured in the shape of thin walls with a length of 100 mm and a height of 80 mm. Two welding speeds were chosen for this experiment–13.3 mm/s and 20.0 mm/s corresponding to the following heat inputs: 120 J/mm and 80 J/mm. The gas metal arc welding (GMAW) method was used for the build-up of the specimens in the cold arc pulse mode. The structure of the specimens was studied using X-ray diffraction (XRD) analysis carried out with CuKα radiation with a wavelength of 1.5406 Ǻ, optical microscopy, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDX). Furthermore, the Vickers hardness of the samples was determined using a ZwickRoell DuraScan 10/20 G5 unit at a force of 1 N. A preferred crystallographic orientation towards the (200) plane was observed in all cases, however a vastly textured structure was observed with inclusions of peaks in the (111), (220), and (311) crystallographic planes. The full width at half maximum (FWHM) of samples taken from different stages of build-up was calculated indicating an increase of the dislocation density at the more advanced stages of specimen growth. Despite that an increase of the hardness was observed towards the top of both specimens. This is attributed to the change in the structure of the αAl + Si formations from an irregular one at the bottom of the specimens, towards a fibrous one at the top. The results are discussed in regard to the optimization of the build-up process during wire arc additive manufacturing (WAAM).