The energy crisis in Pakistan has crippled the country’s economy with an energy shortfall reaching up to 6000 MW. Fortunately, Pakistan lies close to the Sun Belt and therefore receives very high irradiation. To this end, in the beginning of 2014 the Pakistani government sanctioned a solar photovoltaic project namely Quaid-e-Azam Solar Park which was rated at 1000 MW. In this study, a cost benefit analysis for the Quaid-e-Azam Solar Park has been developed. The model uses RETScreen software. In fact, a literature review pointed out that most of the previous research work with reference to cost benefit analysis for solar projects has been mainly carried out on smaller power plants. The outcome of the study shows promising results with the simple payback period coming out at 5.6 years. Furthermore, this analysis can serve as guideline for future solar photovoltaic projects in Pakistan and can help in the development and utilization of the huge solar potential of the country, thus aiding in the reduction of energy shortage. In its proposal, our research is unique and innovative in the Pakistani context. The results aim to serve as a guideline for decision makers and researchers interested in this topic.

Hotspots pose a significant long-term reliability challenge in photovoltaic (PV) modules that can have a detrimental impact on the efficiency, safety, and financial viability of a PV system. This paper aims to evaluate the endurance of hotspot stress in pristine and prestressed glass–glass (GG) modules. The accelerated prestressing was conducted for 600 thermal cycles (TC600) to represent decades of field exposure. GG modules are quickly becoming an alternative to the traditional glass–backsheet (GB) modules that have been the industry standard. Unlike other conventional studies that subject only pristine modules to hotspot stress, this paper evaluates the performance of an accelerated/simulated field-aged GG module (using TC600) and a pristine GG module. Pre- and post-characterizations were performed before and after each test to determine changes in electrical performance and observe any defects in GG modules. During the hotspot test, an approximately 200 °C maximum cell temperature was observed with a cell shading of 25% (the worst-case shading ratio). After the hotspot test, electroluminescence imaging indicated that most cells in the prestressed GG module exhibited severe damage whereas no significant defects were evident in the pristine GG module where the prestressed GG module degraded 8.2% and the pristine GG module degraded 1.5% in maximum power. These findings are critical for the industry, considering that GG bifacial modules will dominate the market.

Investigation and Comparison of DC and AC Nanogrid Networks using MATLAB/Simulink

Potential induced degradation of the polarization type (PID-p) can reduce module performance in a relatively short period of time. PID-p can occur at both voltage polarities, but most studies are focused on degradation under a negative bias. This paper uses commercial bifacial passivated emitter and rear contact (PERC) cells within a monofacial glass-backsheet module construction to evaluate the impact of PID-p under a positive bias on the front side. Using the aluminum-foil (Al-foil) method, the module was stressed for PID in an environmental chamber. After the stress, the maximum power (Pmax) showed a decline of 3.1% at 1000 W/m ² and 6.2% at 200 W/m ² . Recovery under light was also investigated. Complete recovery was observed at high irradiance, while a partial recovery was seen at lower irradiance. The outcomes of this study can help in understanding PID-p degradation under a positive bias and its recovery under the light.