Carbon-based materials have been widely explored as electromagnetic (EM) wave absorbing materials with specific surface areas and low density. Herein, novel porous carbon/SiOC ceramic composites materials (porous C/sp-SiOC) were prepared from the binary mixture, which used the low cost pitch as carbon resource and the polysilylacetylene (PSA) as SiOC ceramic precursor. With the melt-blending-phase separation route, the PSA resin formed micro-spheres in the pitch. Then, numerous SiOC ceramic micro-spheres were generated in porous carbon matrices during the pyrolysis process. By changing the percent of SiOC, the microstructure and wave absorption of porous C/sp-SiOC composites could be adjusted. The synergistic effect of the unique structure, the strong interfacial polarization, and the optimized impedance matching properties contributed to the excellent absorption performance of porous C/sp-SiOC composites. The minimum reflection loss for porous C/sp-SiOC absorber reached −56.85 dB, and the widest effective bandwidth was more than 4 GHz with a thickness of only 1.39 mm. This presented research provides an innovative and practical approach to developing high-performance porous carbon-based microwave absorption materials from green chemistry.

Cf/C-SiC composites have become the preferred material for high-temperature load-bearing applications because of their low density, high strength, and excellent thermal-physical properties. Due to the composite’s poor sintering performance, the sintering temperature and pressure required for the preparation of Cf/C-SiC by traditional methods are also relatively high, which limits its engineering application. Herein, based on the precursor-derived ceramic route and C/C composites material preparation process, a binary binder (coal pitch and polysilylacetylene) is developed, which combines a carbon source, SiC precursor, and semi-ceramic SiC filler organically. Then, the SiC phase was successfully introduced into C/C composites by the slurry impregnation-hot pressing sintering method. The prepared Cf/C-SiC composites showed good mechanical properties, with a density of 1.53 g/cm³ and a bending strength of 339 ± 21 MPa. Moreover, the effects of the binary binder on the microstructure, density, and mechanical properties of Cf/C-SiC composites were investigated. This work provides a novel and effective approach to fabricating Cf/C-SiC composites with low density and high strength.