Rechargeable batteries are attractive power storage equipment for a broad diversity of applications. Lithium-ion (Li-ion) batteries are widely used the superior rechargeable battery in portable electronics. The increasing needs in portable electronic devices require improved Li-ion batteries with excellent results over many discharge-recharge cycles. One important approach to ensure the electrodes’ integrity is by increasing the storage capacity of cathode and anode materials. This could be achieved using nanoscale-sized electrode materials. In the article, we review the recent advances and perspectives of carbon nanomaterials as anode material for Lithium-ion battery applications. The first section of the review presents the general introduction, industrial use, and working principles of Li-ion batteries. It also demonstrates the advantages and disadvantages of nanomaterials and challenges to utilize nanomaterials for Li-ion battery applications. The second section of the review describes the utilization of various carbon-based nanomaterials as anode materials for Li-ion battery applications. The last section presents the conclusion and future directions.

Herein, we report the effect of synthesis temperature on the morphologies, optical and electronic properties of magnesium oxide (MgO) nanostructures. The MgO nanostructures were synthesized at different temperatures, i.e., 100 °C, 300 °C, and 600 °C by simple chemical reaction process and their morphology, particle size, optical, and electrical properties were examined by different techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and UV-Vis. spectroscopy. The morphological investigations revealed that various morphologies of MgO nanostructures, i.e., nanoparticles, nanosheet networks, and nanoneedles were synthesized at 100 °C, 300 °C, and 600 °C. The XRD results confirmed that with increasing the synthesis temperature, the crystallinity of the synthesized nanostructures increases. Further, the dielectric properties and AC conductivity at various frequencies for MgO nanostructures were studied which revealed that the dielectric losses decrease with increase in frequency and temperature. In addition, the observed band gap decreases from 4.89 eV to 4.438 eV (100 °C to 600 °C) representing its increase in the conductivity.

The growth of the textile industry results in a massive accumulation of dyes on water. This enormous rise in pigments is the primary source of water pollution, affecting the aquatic lives and our ecosystem balance. This study aims to notify the fabrication of neodymium incorporated copper oxide (Nd₂O₃ doped CuO) nanoparticles by combustion method for effective degradation of dye, methylene blue (MB). X-ray diffraction (XRD), Field emission Scanning electron microscopy (FESEM), Zeta potential have been applied for characterization. Photocatalyst validity has been evaluated for methylene blue degradation (MB). Test conditions such as time of contact, H₂O₂, pH, and photo-Fenton have been modified to identify optimal degradation conditions. Noticeably, 7.5% Nd₂O₃ doped CuO nanoparticle demonstrated the highest photocatalytic efficiency, up to 90.8% in 80 min, with a 0.0227 min⁻¹ degradation rate. However, the photocatalytic efficiency at pH 10 becomes 99% with a rate constant of 0.082 min⁻¹. Cyclic experiments showed the Nd₂O₃ doped CuO nanoparticle’s stability over repeated use. Scavenge hydroxyl radical species responsible for degradation using 7.5% Nd₂O₃ doped CuO nanoparticles have been investigated under visible irradiation.