In-situ temperature and strain during copper casting process were monitored for the first time based on regenerated fiber Bragg grating (RFBG) sensors, with the maximum temperature up to 1100 $^{\circ }$ C and the largest compressive strain approximately −14 000 $\mu$ $\varepsilon$ . A generalized fifth-order polynomial calibration function was used to convert the measured Bragg wavelengths from RFBG into temperature values. With an RFBG temperature sensor array, the temperature distribution as a function of time was obtained, revealing how the temperature gradient changed during the casting process. In-situ strain was measured by an RFBG strain sensor in direct contact with copper, showing the strain progression inside the copper at different temperatures during the casting. The RFBG-based in-situ monitoring method provides a new way for measuring multiple parameters in high temperature casting, which can be used for improving the design of the casting mold and upgrading the casting quality. Furthermore, our investigation lays a good foundation for fiber-embedded smart metal structures as it shows that fiber sensors can be embedded in copper casts without special surface treatment.

An array of regenerated fiber Bragg gratings (RFBGs) was employed to monitor the temperature distribution during an aluminum cast process. Significant temperature gradients in the cast part were observed during the cooling and solidification period. The direction and velocity of the solidification front was revealed by the temperature data obtained by the RFBGs at different measurement points. A generalized calibration curve was established and applied to the RFBG array, avoiding the need of individual calibration measurements of each sensor element of the array. Temperatures measured using the RFBGs and a thermocouple placed in a reference arm of the mold showed excellent agreements and indicated that no thermal drift of the RFBGs sensor elements occurred during the casting. The RFBG measurements were carried out with only a single fiber, which reduced the amount of lead cables in the melt and hence minimized the sensor-induced disturbances to the casting process. In addition, the limited number of cables enables the RFBG sensors to be deployed in small and complex cast geometries. Multipoint temperature sensors based on RFBG arrays can become important tools to improve the quality of casting processes.

In this study, the response of regenerated fiber Bragg gratings (RFGBs) to axial forces was investigated in a temperature range from room temperature to 900 °C. For the first time, the transition from pure elastic to viscoelastic behavior around 700 °C of a standard SMF28 optical fiber was measured with an inscribed RFBG. An elastic model with linear temperature dependencies of Young’s modulus and Poisson’s ratio was established, and showed good agreement with the measurements up to temperatures of ∼500 °C. In the temperature range up to 900 °C, the RFBG response could be well described with a simple, single-material approach and a Burgers model that consists of a Kelvin and a Maxwell part. Based on the elastic parameter of the Maxwell part, the temperature-dependent force sensitivity of the RFBG was determined, and it showed a linear decrease in the range from room temperature to ∼500 °C, constant values in the range between ∼500 °C and ∼600 °C, and a strong increase at higher temperatures. While fulfilling the condition to operate in the elastic domain of the silica fiber, the investigations demonstrate that RFBGs can be used as force sensors up to temperatures of ∼600 °C - the range in which temperature-dependent force sensitivities have to be considered. The temperature-dependent parameters of the effective single-material model (elastic and viscoelastic part) are essential to describe the effective mechanical behavior of the optical fiber at high temperatures.

In this study, the response of fiber Bragg gratings (FBGs) embedded in cast aluminum parts under thermal and mechanical load were investigated. Several types of FBGs in different types of fibers were used in order to verify general applicability. To monitor a temperature-induced strain, an embedded regenerated FBG (RFBG) in a cast part was placed in a climatic chamber and heated up to 120 ${}^{\circ }\mathrm{C}$ within several cycles. The results show good agreement with a theoretical model, which consists of a shrink-fit model and temperature-dependent material parameters. Several cast parts with different types of FBGs were machined into tensile test specimens and tensile tests were executed. For the tensile tests, a cyclic procedure was chosen, which allowed us to distinguish between the elastic and plastic deformation of the specimen. An analytical model, which described the elastic part of the tensile test, was introduced and showed good agreement with the measurements. Embedded FBGs - integrated during the casting process - showed under all mechanical and thermal load conditions no hysteresis, a reproducible sensor response, and a high reliable operation, which is very important to create metallic smart structures and packaged fiber optic sensors for harsh environments.

In recent years, the observation of the behaviour of components during the production process and over their life cycle is of increasing importance. Structural health monitoring, for example of carbon composites, is state-of-the-art research. The usage of Fibre Bragg Gratings (FBGs) in this field is of major advantage. Another possible area of application is in foundries. The internal state of melts during the solidification process is of particular interest. By using embedded FBGs, temperature and stress can be monitored during the process. In this work, FBGs were embedded in aluminium alloys in order to observe the occurring strain. Two different FBG positions were chosen in the mould in order to compare its dependence. It was shown that FBGs can withstand the solidification process, although a compression in the range of one percent was measured, which is in agreement with the literature value. Furthermore, different lengths of the gratings were applied, and it was shown that shorter gratings result in more accurate measurements. The obtained results prove that FBGs are applicable as sensors for temperatures up to 740 °C.

A 20 mm long 3D-FEM model of a Panda fiber was developed to improve the understanding of multi-parameter sensing in attached or embedded polarization maintaining (PM) fibers. Previously unknown but for FEM modeling critical material parameters of the fiber's stress applying parts (SAP) were determined by a combination of measurements and simulations. The methodology gave evidence of a doping concentration of about 24 mole-% B2O3 in the SAPs for the specific type of PM fiber used. The model was evaluated for axial strains up to 1600 μstrain, axial stress up to 170 MPa and in a temperature range from -40°C to 160°C. The simulated changes in the Bragg wavelengths of the slow and the fast axes and the change of their separation due to applied axial strain, stress and temperature variations were in good agreement with measured data. A reliable 3D-FEM model of an FBG in a Panda fiber is now available that can be integrated into lager FEM models of embedded or surface-glued sensors fibers of type Panda. The model can be used to predict the influences of any arbitrary mechanical loads on an FBG in a Panda-type fiber at different temperatures.