Micro-optical gyroscopes (MOGs) place a range of components of the fiber-optic gyroscope (FOG) onto a silicon substrate, enabling miniaturization, low cost, and batch processing. MOGs require high-precision waveguide trenches fabricated on silicon instead of the ultra-long interference ring of conventional F OGs. In our study, the Bosch process, pseudo-Bosch process, and cryogenic etching process were investigated to fabricate silicon deep trenches with vertical and smooth sidewalls. Different process parameters and mask layer materials were explored for their effect on etching. The effect of charges in the Al mask layer was found to cause undercut below the mask, which can be suppressed by selecting proper mask materials such as SiO₂. Finally, ultra-long spiral trenches with a depth of 18.1 μm, a verticality of 89.23°, and an average roughness of trench sidewalls less than 3 nm were obtained using a cryogenic process at −100 °C.

In this paper, we proposed an efficient and high-precision process for fabricating large-area microlens arrays using thermal reflow combined with ICP etching. When the temperature rises above the glass transition temperature, the polymer cylinder will reflow into a smooth hemisphere due to the surface tension effect. The dimensional differences generated after reflow can be corrected using etching selectivity in the following ICP etching process, which transfers the microstructure on the photoresist to the substrate. The volume variation before and after reflow, as well as the effect of etching selectivity using process parameters, such as RF power and gas flow, were explored. Due to the surface tension effect and the simultaneous molding of all microlens units, machining a 3.84 × 3.84 mm² silicon microlens array required only 3 min of reflow and 15 min of ICP etching with an extremely low average surface roughness Sa of 1.2 nm.

In this paper, a high-precision, low-cost, batch processing nanoimprint method is proposed to process a spherical microlens array (MLA). The nanoimprint mold with high surface precision and low surface roughness was fabricated by single-point diamond turning. The anti-sticking treatment of the mold was carried out by perfluorooctyl phosphoric acid (PFOPA) liquid deposition. Through the orthogonal experiment of hot embossing with the treated mold and subsequent inductively coupled plasma (ICP) etching, the microstructure of MLA was transferred to the silicon substrate, with a root mean square error of 17.7 nm and a roughness of 12.1 nm Sa. The average fitted radius of the microlens array units is 406.145 µm, which is 1.54% different from the design radius.