The topic of sustainability of reinforced concrete structures is strictly related with their durability in aggressive environments. In particular, at equal environmental impact, the higher the durability of construction materials, the higher the sustainability. The present review deals with the possible strategies aimed at producing sustainable and durable reinforced concrete structures in different environments. It focuses on the design methodologies as well as the use of unconventional corrosion-resistant reinforcements, alternative binders to Portland cement, and innovative or traditional solutions for reinforced concrete protection and prevention against rebars corrosion such as corrosion inhibitors, coatings, self-healing techniques, and waterproofing aggregates. Analysis of the scientific literature highlights that there is no preferential way for the production of “green” concrete but that the sustainability of the building materials can only be achieved by implementing simultaneous multiple strategies aimed at reducing environmental impact and improving both durability and performances.

The critical chloride threshold is a key parameter in the service life design of reinforced concrete structures exposed to chloride-bearing environments. This paper investigates the role of concrete composition, and particularly the effect of supplementary cementing materials, on the chloride threshold. To simulate real exposure conditions, ponding tests were carried out on reinforced concrete specimens with bars in free corrosion conditions and corrosion initiation was detected through corrosion potential and corrosion rate measurements. After two and a half years, the ponding was followed by an ageing period and the initiation of corrosion was further detected with anodic potentiostatic polarisation tests. Results of the tests showed several limitations of the approach based on chloride penetration and monitoring of free corrosion parameters to investigate the chloride threshold. In spite of this, a possible role of natural pozzolan and coal fly ash additions in leading to higher values of the chloride threshold and ground limestone in promoting lower values of the chloride threshold could be observed.