Anticounterfeiting of goods is an urgent need both for luxury and cheap everyday life products. Their identification is usually based on overt technologies as printed codes, easy to produce but to be cloned as well. In this work, a standard QR‐code printed on office paper but hidden by a plasmonic multilayer system is exploited. The covert label is then protected by a peculiar reading mechanism, which is only possible in specific illumination conditions. The overall photonic structure consisting of the metal –insulator –metal –insulator, the printed random QR code and the paper substrate results in a strong physical unclonable function (PUF) that provides a multi‐level identification and authentication of goods ensuring uniqueness of nominally quasi‐identical tags and resistance to tampering/cloning attacks. The proposed paper‐based camouflage physical unclonable function (PC‐PUF) can be easily fabricated by low cost and large area techniques paving the way for an easy integration in an industrial supply‐chain as tags devoted to protect consumer merchandises.

In this study, a method is presented to fabricate optical fingerprint‐like patterns. The method relies on the use of commercially available chiral nematic liquid crystals (CNLCs) confined in microspheres. The peculiar optical texture is obtained by applying a high‐frequency voltage to the micrometric objects able to distort the molecular director orientation. The texture can be stabilized by doping the CNLC with photosensitive materials. Each microsphere shows a different fingerprint‐like pattern that is generated in a completely random manner making this procedure suitable to create physical unclonable functions (PUFs) keys. The optical patterns can be stored to create an artificial fingerprints database or they can be used to fabricate electroluminescent labels to be exploited as complex anti‐counterfeiting devices. An authentication software is developed and used to test the robustness of the proposed anti‐counterfeiting system.

Multilevel anticounterfeiting Physical Unclonable Function (PUF) tags based on thin film of silver (Ag), Zinc Oxide (ZnO) and PolyVinylPyrrolidone (PVP), are experimentally demonstrated and validated. We exploit the low adhesion of silver to glass and consequent degradation during ZnO deposition to induce morphological randomness. Several photographs of the tag surfaces have been collected with different illumination conditions and using two smartphones of diverse brand. The photos were analyzed using an image recognition algorithm revealing low common minutiae for different tags. Moreover, the optical response reveals peculiar spectra due to labels of plasmonic nature. The proposed systems can be easily fabricated on large areas and represent a cost-effective solution for practical protection of objects.

Counterfeiting poses an ever‐growing challenge, driving the need for innovative anti‐counterfeiting strategies and technologies. Many solutions focus on tags characterized by optical features that are camouflaged to the human eye, thus discouraging scammers. In this paper, a QR code is printed using a commercial printer on a thin plastic foil previously coated by a specific nanocavity consisting of a metal‐insulator‐metal‐insulator (MIMI) multilayer, that possesses unique features in terms of light transmission and reflection, due to its specific design. A thin layer of polymer dispersed liquid crystals (PDLC), is fabricated to camouflage the QR code that becomes, then, readable only under specific thermal conditions. Two anti‐counterfeiting tags were fabricated, each using a distinct nematic liquid crystal (NLC) with its own nematic‐isotropic transition temperature. The combination of the unique optical properties of NLCs and optical nanocavities results in the creation of a new type of tags showing two different encoding levels. Stability tests such as immersion in water, bending test, and prolonged heating have been performed ensuring the long‐term stability of the tags. The realized two security‐level anti‐counterfeiting tags are cost‐effective, straightforward to manufacture and, thanks to their flexibility, can be easily integrated into packaging and products.

Membrane modification is becoming ever more relevant for mitigating fouling phenomena within wastewater treatment applications. Past research included a novel low-fouling coating using polymerizable bicontinuous microemulsion (PBM) induced by UV-LED polymerization. This additional cover layer deteriorated the filtration capacity significantly, potentially due to the observed high pore intrusion of the liquid PBM prior to the casting process. Therefore, this work addressed an innovative experimental protocol for controlling the viscosity of polymerizable bicontinuous microemulsions (PBM) before casting on commercial ultrafiltration (UF) membranes. Prior to the coating procedure, the PBM viscosity modulation was carried out by controlled radical polymerization (CRP). The regulation was conducted by introducing the radical inhibitor 2,2,6,6-tetramethylpiperidine 1-oxyl after a certain time (CRP time). The ensuing controlled radical polymerized PBM (CRP-PBM) showed a higher viscosity than the original unpolymerized PBM, as confirmed by rheological measurements. Nevertheless, the resulting CRP-PBM-cast membranes had a lower permeability in water filtration experiments despite a higher viscosity and potentially lower pore intrusion. This result is due to different polymeric structures of the differently polymerized PBM, as confirmed by solid-state nuclear magnetic resonance (NMR) investigations. The findings can be useful for future developments in the membrane science field for production of specific membrane-coating layers for diverse applications.