This article demonstrates changes in the structures of poly (3,4-ethylene dioxythiophene): polystyrene sulfonate (PEDOT: PSS) with the addition of organic additives. The mechanisms of PEDOT: PSS are analyzed using X-ray photoelectron spectroscopy (XPS), cross-sectional images obtained from scanning electron microscopy (SEM), and contact angles. In this paper, a bond-breaking reaction and phase separation are successfully found to occur between PEDOT: PSS molecules and the organic additives. Our research also finds that this bond-breaking reaction and phase separation exist in the PEDOT: PSS–sorbitol–maltitol film at the same time. The addition of organic additives will improve the optical properties and the moisture stability of PEDOT: PSS films.

In recent years, the study of organic–inorganic halide perovskite as an optoelectronics material has been a significant line of research, and the power conversion efficiency of solar cells based on these materials has reached 25.5%. However, defects on the surface of the film are still a problem to be solved, and oxygen plasma is one of the ways to passivate surface defects. In order to avoid destroying the methylammonium lead iodide (MAPbI₃), the influence of plasma powers on film was investigated and the cesium triiodide (CsPbI₃) quantum dots (QDs) were doped into the film. In addition, it was found that oxygen plasma can enhance the mobility and carrier concentration of the MAPbI₃ film.

This article demonstrates the change of structural and optical properties of poly (3,4-ethylene dioxythiophene): polystyrene sulfonate (PEDOT: PSS) by organic additive and acid treatment. The addition of sorbitol and maltitol can disperse the micelles of PEDOT: PSS. The mechanism of the bond-breaking reaction was investigated and a model for the bond-breaking reaction is also proposed. Furthermore, multiple formic acid treatments were found to reduce the PSS content of PEDOT: PSS, resulting in an enhancement in conductivity (4.2 × 10⁴ S/m).

In this study, adding CsPbI₃ quantum dots to organic perovskite methylamine lead triiodide (CH₃NH₃PbI₃) to form a doped perovskite film filmed by different temperatures was found to effectively reduce the formation of unsaturated metal Pb. Doping a small amount of CsPbI₃ quantum dots could enhance thermal stability and improve surface defects. The electron mobility of the doped film was 2.5 times higher than the pristine film. This was a major breakthrough for inorganic quantum dot doped organic perovskite thin films.

In this study, the inorganic perovskite cesium lead triiodide (CsPbI₃) quantum dots (QDs) produced by hot-injection method were added into the hybrid perovskite methylamine lead triiodide (CH₃NH₃PbI₃; MAPbI₃) to form composite perovskite film. It is not easy for argon (Ar) to react with perovskite. Therefore, argon plasma was used to optimize the properties of the surface. However, methylamine lead triiodide molecular will be degraded by excessive wattage. Therefore, the influence of plasma power acting on composite perovskite film was investigated. The experimental results show that the light absorption capacity can be increased by argon plasma power of 140 watt (W) acting on the surface of films because organic impurities are removed and surface morphology of film is changed.