This work presents the evaluation of the interlayer temperature (IT) with travel speed (TS) combined effect for a given wire feed speed (WFS) on operational, geometrical, and metallurgical features of thin walls with the same width deposited by wire arc additive manufacturing (WAAM) with a low alloy steel, using or not active cooling. A preliminary experimental design was carried out to define a range of IT that could prevent the molten pool from running down and, then, be used in the main experimental design. The main tests were planned and performed to find different IT and TS combinations for a given WFS capable of depositing walls with the same target effective wall width. After selecting the parameters, six walls were deposited, three under natural cooling (NC) and three under near immersion active cooling (NIAC). A more significant temperature variability along the layer length (ΔT/ΔLL) is observed in increasing IT-TS combination and under NIAC. Regardless of the cooling approach, a worse surface aspect was observed with lower IT and TS. However, NC or NIAC do not affect the wall width (effective or external) or the layer height. On the other hand, they are affected by the IT with TS combination. A shorter production time was obtained on the walls with NIAC and higher IT-TS. No marked microstructural differences were observed comparing the walls, regardless of the cooling approach. However, microstructure tempering (hardness reduction) was observed in the walls deposited with NC using higher IT levels.

Significant efforts have been spent determining or monitoring interlayer temperatures (IT) to increase quality in Wire Arc Additive Manufacturing (WAAM). However, an uneven thermal profile in the wall and a temperature gradient along the layer length are expected after a thin wall layer deposition, questioning the effectiveness of IT and its measuring approaches. After identifying the holistic meaning of IT, this work aimed at confronting two strategies using infrared pyrometers, elucidating their advantages and limitations for both open and closed-loop control. The proposed Upper and Sideward Pyrometer strategies were presented in detail and then assessed at different distances from the heat source. A calibration procedure was proposed. The results confirmed the existence of a natural temperature gradient along the wall. In addition, they showed how differently the arc heat affects the measured points (in intensity and steadiness) according to the strategy. Therefore, the interlayer temperature measured at a specific point on a part manufactured by WAAM should be taken as a reference and not an absolute value; the absolute value changes according to the measuring approach, sensor positioning and calibration. Using a temperature reference, both strategies can be used in open-loop control to reach repeatability (geometrical and metallurgical) between layers. However, the Sideward Pyrometer strategy is more recommended for feedback control of production, despite being less flexible.

The main objective of this work was to propose and evaluate a methodology for shielding-gas selection in additive manufacturing assisted by wire arc additive manufacturing (WAAM) with an austenitic stainless steel as feedstock. To validate the proposed methodology, the impact of multi-component gases was valued using three different Ar-based blends recommended as shielding gas for GMA (gas metal arc) of the target material, using CMT (cold metal transfer) as the process version. This assessment considered features that potentially affect the building of the case study of thin walls, such as metal transfer regularity, deposition time, and geometrical and metallurgical characteristics. Different settings of wire-feed speeds were conceived to maintain a similar mean current (first constraint for comparison’s sake) among the three gas blends. This approach implied different mean wire-feed speeds and simultaneously forced a change in the deposition speed to maintain the same amount of material deposited per unit of length (second comparison constraint). The composition of the gases affects the operational performance of the shielding gases. It was concluded that by following this methodology, shielding-gas selection decision-making is possible based on the perceived characteristics of the different commercial blends.

The successful and efficient production of parts with specific features by Wire + Arc Additive Manufacturing (WAAM) strongly depends on the selection of proper and typically interrelated deposition parameters. This task might be particularly challenging in the making of thin walls, which might be highly impacted by processing conditions and heat accumulation. In this context, this study aims at expanding the work envelope and optimizing the parametric conditions in WAAM with relative density and surface aspects of the preforms as quality constraints. The experimental approach was based on the deposition of thin Al5Mg walls by the CMT process on its standard welding setup and with an active cooling technique to enhance the deposition robustness. Internal voids were estimated by Archimedes’ method. The surface quality of the walls was assessed through the visual aspect and the surface waviness by cross-section analysis. All the conditions presented relative density higher than 98%. The upgrade of the standard welding hardware to WAAM purposes through the addition of a supplementary shielding gas nozzle to the torch and the intensity of the heat sinking from the part significantly expanded the process work envelope, with its applicability being successfully demonstrated with multi-objective optimization. To sum up, a decision-making procedure is presented towards achieving intended preform quality.

(2018). Nickel overlay deposited by MIG welding and cold wire MIG welding. Welding International: Vol. 32, No. 9, pp. 588-598.