Optimization of thin film uniformity is an important aspect for large-area coatings, particularly for optical coatings where error tolerances can be of the order of nanometers. Physical vapor deposition is a widely used technique for producing thin films. Applications include anti-reflection coatings, photovoltaics etc. This paper reviews the methods and simulations used for improving thin film uniformity in physical vapor deposition (both evaporation and sputtering), covering characteristic aspects of emission from material sources, projection/mask effects on film thickness distribution, as well as geometric and rotational influences from apparatus configurations. Following the review, a new program for modelling and simulating thin film uniformity for physical vapor deposition was developed using MathCAD. Results from the program were then compared with both known theoretical analytical equations of thickness distribution and experimental data, and found to be in good agreement. A mask for optimizing thin film thickness distribution designed using the program was shown to improve thickness uniformity from ±4% to ±0.56%.

To meet the requirements for lightweight, miniaturized dispersive optical systems for space applications, linear variable filters with a high transmittance and spatial dispersion coefficient are proposed. The filters were produced with dual ion beam sputtering, where a single layer thickness variation was achieved with a deposition rate adjustment based on a linear variable correction formula. A linear variable trend matching method was used to correct the film thickness based on the reduction of the mismatch error between two materials: Ta₂O₅ and SiO₂. The influence of the spectral and spatial measuring average effects was addressed by sampling the spot size optimization. This paper presents an all-dielectric linear variable filter that operates between 520 and 1000 nm, with an excellent linear dependence of 40 nm/mm over 12 mm. The linear variable filter possessed a 2.5% bandwidth, and its transmittance was found to be >80% at the central wavelength of the band, with a 0.1% transmittance in the cut-off region. These results indicate great potential for optical devices for space applications, and the developed process has good reproducibility and stability.

Driven by the rapid innovation of science and technology and industrial manufacturing technology, virtual reality display technology has developed rapidly. At present, the application of virtual reality display technology is expanding in many fields such as military, medical, aviation and education. This paper analyzes the imaging principle of the human vision system and the optical performance requirements of VR heads-up display, summarizes the current design scheme of VR heads-up optical imaging system, focuses on the principle and index parameters of each optical system, and compares the advantages and disadvantages of different schemes. The development prospects and directions of virtual reality headset displays are also prospected.

TiO₂ deposition using separate regions for sputtering and oxidation is not well investigated. We optimized process parameter for such as oxygen flow and microwave power to produce high quality TiO₂ filters for Stereo/3D imaging applications. This deposition technique was chosen for its unique advantages: high deposition rates while increasing the probability of obtaining stoichiometric oxides, reduces possibility of target poisoning and provides better stability of process. Various characterization methods, such as scanning electron microscopy (SEM), atomic force microscopy (AFM), Raman, X-ray diffraction (XRD), transmission spectroscopy, were used in compliment to simulations for detailed analysis of deposited TiO₂ thin films. Process parameters were optimized to achieve TiO₂ films with low surface scattering and absorption for fabricating multi-passbands interference filter for 3D glasses. From observations and quantitative analysis of surfaces, it was seen that surface roughness increases while oxygen flow or microwave power increases. As the content of anatase phase also increases with higher microwave power and higher oxygen flow, the formation of anatase grains can cause higher surface roughness. Optical analysis of samples validates these trends and provided additional information for absorption trends. Optimized parameters for deposition process are then obtained and the final fabricated 3D glasses filters showed high match to design, within 0.5% range for thickness error.

Magnesium fluoride (MgF₂) materials are commonly used for near/medium infrared anti-reflection optical coatings due to their low refractive index and wide-range transparency. Ion assistant deposition is an important technique to increase the density of MgF₂ and reduce absorption around 2.94 µm caused by high porosity and moisture adsorption. However, the excessive energy of Argon ion will induce a color center and; therefore, lead to UV/Visible absorption. In this paper, oxygen ion was introduced to reduce the color center effect in MgF₂ thin film deposited using electron beam evaporation with ion assistant. The films were deposited on Bk7 and single crystal silicon substrates under various oxygen ion beam currents. The microstructure, optical constant, film density, stress, and adhesion are investigated, including the absorption properties at the infrared hydroxyl (–OH) vibration peak. The results show that as the oxygen ion beam current increases, the absorption value at the position of the infrared OH vibration, defects, and stress of the film decrease, while the refractive index increases. However, MgF₂ has poor adhesion using oxygen ion-assisted deposition. Thin MgF₂ film without ion beam assistant was used as adhesive layer, high density, and low absorption MgF₂ film with good adhesion was obtained.