With advancements in the automated industry, electromagnetic inferences (EMI) have been increasing over time, causing major distress among the end-users and affecting electronic appliances. The issue is not new and major work has been done, but unfortunately, the issue has not been fully eliminated. Therefore, this review intends to evaluate the previous carried-out studies on electromagnetic shielding materials with the combination of Graphene@Iron, Graphene@Polymer, Iron@Polymer and Graphene@Iron@Polymer composites in X-band frequency range and above to deal with EMI. VOSviewer was also used to perform the keyword analysis which shows how the studies are interconnected. Based on the carried-out review it was observed that the most preferable materials to deal with EMI are polymer-based composites which showed remarkable results. It is because the polymers are flexible and provide better bonding with other materials. Polydimethylsiloxane (PDMS), polyaniline (PANI), polymethyl methacrylate (PMMA) and polyvinylidene fluoride (PVDF) are effective in the X-band frequency range, and PDMS, epoxy, PVDF and PANI provide good shielding effectiveness above the X-band frequency range. However, still, many new combinations need to be examined as mostly the shielding effectiveness was achieved within the X-band frequency range where much work is required in the higher frequency range.

Erosion caused by the repeated impact of particles on the surface of a substance is a common wear method resulting in the gradual and continual loss of affected objects. It is a crucial problem in several modern industries because the surfaces of various products and materials are frequently subjected to destructively erosive situations. Polymers and their hybrid materials are suitable, in powdered form, for use as coatings in several different applications. This review paper aims to provide extensive information on the erosion behaviors of thermoset and thermoplastic neat resin and their hybrid material composites. Specific attention is paid to the influence of the properties of selected materials and to impingement parameters such as the incident angle of the erodent, the impact velocity of the erodent, the nature of the erodent, and the erosion mechanism. The review further extends the information available about the erosion techniques and numerical simulation methods used for wear studies of surfaces. An investigation was carried out to allow researchers to explore the available selection of materials and methods in terms of the conditions and parameters necessary to meet current and future needs and challenges, in technologically advanced industries, relating to the protection of surfaces. During the review, which was conducted on the findings in the literature of the past fifty years, it was noted that the thermoplastic nature of composites is a key component in determining their anti-wear properties; moreover, composites with lower glass transition, higher ductility, and greater crystallinity provide better protection against erosion in advanced surface applications.

In the present work, the facile thermal decomposition of raw coconut shells was carried out for the exploitation of the role of inert gas in the carbonization process and its role in determining the morphology, crystallographic parameters, and surface area of biochar before activation. The comparative investigation of mesoporous carbonized products synthesized with the muffle and tube furnace was carried out at a similar temperature and an assessment was made with a commercial carbon. The focus of the work was aimed at the interpretation of surface morphology, elemental identification, phase composition, interplanar spacing, full-width half maximum, crystallite size, lateral size, number of layers, dislocation density, microstrain, packing density, crystallinity index, and the specific surface area of the product obtained from two different approaches. It was revealed that the carbonized coconut shell chars obtained from the tube furnace have better characteristics to be activated further for carbon black synthesis. So, the flow of inert gas in a tube furnace is demonstrated to have a key role in improving the attributes of coconut shell chars.

This work aimed to study the thermal and crystalline properties of poly (1,4-phenylene sulfide)@carbon char nanocomposites. Coagulation-processed nanocomposites of polyphenylene sulfide were prepared using the synthesized mesoporous nanocarbon of coconut shells as reinforcement. The mesoporous reinforcement was synthesized using a facile carbonization method. The investigation of the properties of nanocarbon was completed using SAP, XRD, and FESEM analysis. The research was further propagated via the synthesis of nanocomposites through the addition of characterized nanofiller into poly (1,4-phenylene sulfide) at five different combinations. The coagulation method was utilized for the nanocomposite formation. The obtained nanocomposite was analyzed using FTIR, TGA, DSC, and FESEM analysis. The BET surface area and average pore volume of the bio-carbon prepared from coconut shell residue were calculated to be 1517 m²/g and 2.51 nm, respectively. The addition of nanocarbon to poly (1,4-phenylene sulfide) led to an increase in thermal stability and crystallinity up to 6% loading of the filler. The lowest glass transition temperature was achieved at 6% doping of the filler into the polymer matrix. It was established that the thermal, morphological, and crystalline properties were tailored by synthesizing their nanocomposites with the mesoporous bio-nanocarbon obtained from coconut shells. There is a decline in the glass transition temperature from 126 °C to 117 °C using 6% filler. The measured crystallinity was decreased continuously, with the mixing of the filler exhibiting the incorporation of flexibility in the polymer. So, the loading of the filler into poly (1,4-phenylene sulfide) can be optimized to enhance its thermoplastic properties for surface applications.

Erosion caused by the repeated impact of particles on a substance surface is a usual wear method resulting in gradual and continual loss of objects. It is a crucial problem in several modern industries because their surfaces are frequently subjected to destructive erosive situations. Polymers and their hybrid materials include several applications to be used as a coating in the form of powder for different applications. This review paper aims to provide extensive information on the erosion behavior of thermoset and thermoplastic neat resin and their hybrid materials composites. Focus is specifically paid to highlight the influence of properties of selected materials, impingnation parameters such as incident Angle of erodent, impact velocity of erodent, erodent nature, and the erosion mechanism. The review further extends the information about the erosion techniques and numerical simulation methods used for wear studies of surfaces. An investigation has been carried out for researchers to explore the selection of materials and methods in terms of conditions and parameters to meet the current and future needs and challenges for the protection of surfaces of the advanced industries. During review according to the findings achieved from the literature of the past fifty years, it has been noted that the thermoplastic nature of the composite is a key component to determine the anti-wear properties, the composites with lower glass transition, higher ductility, and greater crystallinity can provide better protection to erosion in advance surface applications.