The development of high-filled 3D printing resin necessitates a bonding protocol for dental indirect restorations to achieve optimal bond strength after cementation. This study evaluates shear bond strengths of high-filler 3D printed materials for permanent restorations with various surface treatments. Rodin Sculpture 1.0 (50% lithium disilicate fillers) and 2.0 Ceramic Nanohybrid (>60% zirconia and lithium disilicate fillers) were tested, with Aelite All-Purpose Body composite resin as control. Samples were prepared, post-cured, and sandblasted with alumina (25 µm). Surface roughness was analyzed using an optical profilometer. Two bonding protocols were compared. First, groups were treated with lithium disilicate silane (Porcelain Primer) or zirconia primer (Z-Prime Plus) or left untreated without a bonding agent. Beam-shaped resin cement (DuoLink Universal) specimens were bonded and stored in a 37 °C water bath. Second, additional sets of materials were coated with a bonding agent (All-Bond Universal), either followed by silane application or left untreated. These sets were then similarly stored alongside resin cement specimens. Shear bond tests were performed after 24 h. SEM images were taken after debonding. One-Way ANOVA and post hoc Duncan were performed for the statistical analysis. Rodin 1.0 exhibited increased adhesive failure with silane or zirconia primer coating, but significantly improved bond strengths with bonding agent application. Rodin 2.0 showed consistent bond strengths regardless of bonding agent application, but cohesive failure rates increased with bonding agent and filler coating. In all groups, except for Rodin 1.0 without bonding agent, silane coating increased cohesive failure rate. In conclusion, optimal shear bond strength for high-filler 3D printing materials can be achieved with silane coating and bonding agent application.

Advanced age is a shared risk factor for many chronic and debilitating skeletal diseases including osteoporosis and periodontitis. Mesenchymal stem cells develop various aging phenotypes including the onset of senescence, intrinsic loss of regenerative potential and exacerbation of inflammatory microenvironment via secretory factors. This review elaborates on the emerging concepts on the molecular and epigenetic mechanisms of MSC senescence, such as the accumulation of oxidative stress, DNA damage and mitochondrial dysfunction. Senescent MSCs aggravate local inflammation, disrupt bone remodeling and bone-fat balance, thereby contributing to the progression of age-related bone diseases. Various rejuvenation strategies to target senescent MSCs could present a promising paradigm to restore skeletal aging.

Epoxy resin-based sealers are commonly used for successful endodontic treatment. This study aimed to evaluate the cytotoxicity and genotoxicity of epoxy resin-based sealers under unset and set conditions. Three epoxy resin-based sealers were used: Adseal, AH Plus, and Dia-Proseal. To test cytotoxicity, an agar overlay test and a 3-[4,5-dimethylthiazol-2-yl]-2,5 diphenyl tetrazolium bromide (MTT) assay were performed using unset and set sealers on L929 mouse fibroblasts. The genotoxicity test of the comet assay was performed using the same cell line. Extract dilutions in the culture media were used as test materials for the MTT and comet assays. The comet tail produced by the damaged DNA was calculated by image analyses. Statistical analyses were performed using one-way analysis of variance and Tukey’s post hoc test. Unset sealers did not show defined decolorized areas. Hardened specimens of resin-based sealers showed circular discolored zones in the agar overlay test. Dia-Proseal was the least cytotoxic after hardening. These results were confirmed in the MTT assay. Cell viability was significantly higher in cells treated with hardened sealers in both groups than that in cells treated with freshly mixed sealers in the MTT assay. Unset AH Plus^® and Dia-Proseal™ significantly increased cell viability with decreasing dilution. Adseal™ was the least cytotoxic. Freshly mixed Adseal™ was more genotoxic when freshly mixed than when set. Unset epoxy resin-based sealers were generally more cytotoxic and genotoxic than set materials. Cytotoxicity does not always match the genotoxicity results; therefore, various test tools are required to test toxicity. It is necessary to properly evaluate the toxic effects to establish a biocompatibility test that mimics clinical conditions.